This study investigates the potential of light-burnt dolomite (LBD) as a supplementary cementitious material with ground granulated blast furnace slag (GGBFS) and Ordinary Portland cement (OPC). In this work, LBD was substituted for up to 20% of GGBFS in sodium sulfate-activated slag systems. The effects of LBD incorporation on the flow, setting time, compressive and flexural strength development, and drying shrinkage were explored with, X-ray diffraction and thermogravimetric analyses. LBD incorporation resulted in greater strength development of an alkali-activated slag system. The optimum LBD content for strength development was 10%, regardless of ordinary Portland cement content. In addition, LBD decreased the drying shrinkage, accelerated the hydration process, and induced hydrotalcite formation, which can be attributed to the reactive MgO inside LBD.
Globally, concrete is the most widely used construction material. The composition of concrete plays an important role in controlling its overall performance. Concrete is composed of approximately 70%–80% aggregates, by volume. Therefore, it is mandatory to investigate the effect of aggregates on the performance of concrete. For this purpose, this study investigated the effect of three different coarse aggregates on the mechanical properties, durability, and microstructure of concrete. Concrete specimens were made using aggregates obtained from three regions with different mineralogies. The specimens were also made by replacing cement with silica fume. The specimens were analyzed in terms of compressive, flexural, and splitting tensile strengths, chloride penetration, carbonation, mercury intrusion porosimetry, and scanning electron microscopy. The results demonstrate that the specimens made with rougher coarse aggregates and silica fume had enhanced performance in comparison to those made with smoother aggregates.
The main purpose of this work is to study the effect of saturated black tea waste and perlite on controlling the rapid heat of hydration in high-strength cement mortars at early ages. Tea waste and perlite were investigated as internal curing agents in different mixes. Mortar specimens with two different sizes of tea waste and perlite particles with 1 and 3% by volume of cement were added in different mixes to find their effect on early age hydration. The rising interior temperature, setting times, and strength parameters were evaluated. Results showed that the mix specimens that contained 3% tea waste and perlite particles significantly delayed the hydration process by minimizing internal temperature and extended setting times of different specimens. However, their usage had a slightly adverse impact on compressive and flexural strengths. It was observed that the specimens made with coarser particles of tea waste and perlite were more helpful to control early age rapid hydration than the specimens made with finer particles, whereas the specimens made with finer particles had slightly higher strengths than the specimens made with coarser particles. Hence, the coarser particles are recommended to be used in high-strength mortars to mitigate the early age rapid heat of hydration.
The depletion of natural sand and production of the huge amount of cement in the construction industry are serious threats to the environment, which can be reduced by the utilization of by-products as cement replacement material. In this study, cement was replaced with fly ash up to 45% (by weight). In addition, the natural fine aggregate was replaced with air-cooled blast furnace slag aggregate (here referred to as “slag aggregate”) at a level of 50% and 100% (by weight). Polypropylene fiber was also added, at a dosage of 0.25% of binder weight. Mortar specimens were prepared and analyzed using tests for compressive, flexure, and splitting tensile strength, as well as for microhardness, and ultrasonic pulse velocity. In addition, the specimens were exposed to sulfate solution and investigated for changes in length, mass, and compressive strength. Electron microscopy and X-ray diffraction analysis were performed to examine the microstructure and phase changes of mortar specimens exposed to sulfate solution. The results indicate that mortar specimens made with 50% slag aggregate and 0.25 % fiber showed enhanced mechanical properties. The performance of slag aggregate mortars under sulfate attack was improved significantly.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.