Abstract:Magnesium is electrochemically the most active metal employed in common structural alloys of iron and aluminum. Mg is widely used as a sacrificial anode to provide cathodic protection of underground and undersea metallic structures, ships, submarines, bridges, decks, aircraft and ground transportation systems. Following the same principle of utilizing Mg characteristics in engineering advantages in a decade-long successful R&D effort, Mg powder is now employed in organic coatings (termed as Mg-rich primers) as a sacrificial anode pigment to protect aerospace grade aluminum alloys against corrosion. Mg-rich primers have performed very well on aluminum alloys when compared against the current chromate standard, but the carcinogenic chromate-based coatings/pretreatments are being widely used by the Department of Defense (DoD) to protect its infrastructure and fleets against corrosion damage. Factors such as reactivity of Mg particles in the coating matrix during exposure to aggressive corrosion environments, interaction of atmospheric gases with Mg particles and the impact of Mg dissolution, increases in pH and hydrogen gas liberation at coating-metal interface, and primer adhesion need to be considered for further development of Mg-rich primer technology.

No abstract

No abstract

No abstract

No abstract

No abstract

No abstract

Magnesium-rich primers (MgRP) have generated great interest as a promising alternative to chromium-based primers for the protection of aluminum substrates but their performance during exterior exposure has not been well documented. This paper focuses on the evaluation of MgRP during natural weathering to gain insight into its mineralogical phase transformation and electrochemical nature. Control studies were conducted on Mg and AA2024-T3 coupons. The results indicate that Mg particles in MgRP transform into a variety of hydroxide, carbonate, and hydroxy carbonates. During natural weathering, CO 2 inhibited the dissolution of both Mg and AA2024-T3 as a result of protective carbonate layer formation in the coating.