Low-temperature ceramics based on magnesium calcium phosphate cement are a promising resorbable material for bone tissue restoration with the possibility of functionalization. The replacement of the magnesium Mg2+ ion with a calcium Ca2+ ion at the stage of preparation of the precursor leads to the production of multiphase ceramics containing phases of brushite, monetite, and newberyite, with different dissolution rates. Multiphase ceramics leads to volumetric resorption with preservation of their geometric shape, which was confirmed by the results of an evaluation of the output of magnesium Mg2+ and calcium Ca2+ ions into the contact solution of the ceramics and the X-ray density of ceramic samples during subcutaneous implantation. The combined introduction of sodium pyrophosphate decahydrate and citric acid monohydrate as setting inhibitors neutralizes their insignificant negative effect on the physico-chemical properties of ceramics (strength, pH, porosity), determining the optimal composition. In vivo experiments with setting inhibitors in the composition of ceramics showed a different biological response, affecting the rate of resorption on par with magnesium ions. Preliminary data on biocompatibility and solubility determined magnesium-calcium phosphate ceramics containing additives that regulate setting to be a potential material for bone tissue restoration and a vector for further research, including in orthotopic implantation models.
The rate of resorption of calcium phosphate self-hardening materials for bone regeneration can be changed by changing the phase composition. The Ca3(PO4)2/CaCO3/Ca(H2PO4)2·H2O/Na2HPO4·12H2O system is important for the synthesis of self-curing bioactive materials with variable resorption rates by changing the ratios of the initial components. Cement compositions in twelve figurative points of a four-component composition diagram at a fixed content in the α-Ca3(PO4)2 system were studied with XRD, FTIR, SEM, calorimetric, and volumetric methods to obtain an idea of the effect of composition on solubility in vitro and resorption in vivo. It was found that the presence of the highly resorbable phase of dicalcium phosphate dihydrate in cement and the substitution of phosphate ions with the carbonate ions of hydroxyapatite increased solubility in vitro and resorption in vivo. The obtained results confirm the possibility of changing the solubility of a final product in the Ca3(PO4)2/CaCO3/Ca(H2PO4)2·H2O/Na2HPO4·12H2O system by changing the ratio of the initial components.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.