Thin films of nanostructured silicon (ns-Si : H) were deposited by plasma-enhanced chemical vapor deposition in the presence of silicon nanoparticles at 100 ± C substrate temperature using a silane and hydrogen gas mixture under continuous wave (cw) plasma conditions. The nanostructure of the films has been demonstrated by diverse ways: transmission electron microscopy, Raman spectroscopy, and x-ray diffraction, which have shown the presence of ordered silicon clusters (1-2 nm) embedded in an amorphous silicon matrix. Because of the presence of these ordered domains, the films crystallize faster than standard hydrogenated amorphous silicon samples, as evidenced by electrical measurements during the thermal annealing.
Nanostructured silicon thin films have been deposited by plasma enhanced chemical vapor deposition at low substrate temperature (100 °C) in the presence of silicon nanoparticles. The nanostructure of the films was revealed by transmission electron microscopy, Raman spectroscopy and X-ray diffraction, which showed ordered silicon domains (1–2 nm) embedded in an amorphous silicon matrix. These ordered domains are due to the particles created in the discharge that contribute to the film growth. One consequence of the incorporation of nanoparticles is the accelerated crystallization of the nanostructured silicon thin films when compared to standard a-Si:H, as shown by the electrical characterization during the annealing.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.