This paper presents an experimental result on the effect of particle size of a mixture of ball clay, kaolin, and sawdust on thermal diffusivity of ceramic bricks. A mixture of dry powders of ball clay, kaolin of the same particle size, and sawdust of different particle sizes was mixed in different proportions and then compacted to high pressures before being fired to 950°C. The thermal diffusivity was then determined by an indirect method involving measurement of thermal conductivity, density, and specific heat capacity. The study reveals that coefficient of thermal diffusivity increases with decrease in particle size of kaolin and ball clay but decreases with increase in particle size of sawdust.

In Uganda and Africa at large, up to 90% of the total energy used for food preparation and water pasteurization is from fossil fuels particularly firewood and kerosene which pollute the environment, yet there is abundant solar energy throughout the year, which could also be used. Uganda is abundantly rich in clay minerals such as ball clay, kaolin, feldspar, and quartz from which ceramic substrates were developed. Aluminium films of different thicknesses were deposited on different substrates in the diffusion pump microprocessor vacuum coater (Edwards AUTO 306). The optical reflectance of the aluminium films was obtained using a spectrophotometer (SolidSpec-3700/DUV-UV-VIS-NIR) at various wave lengths. The analysis of the results of the study revealed that the optical reflectance of the aluminium films was above 50% and increased with increasing film thickness and wavelength. Thus, this method can be used to produce reflector systems in the technology of solar cooking and other appliances which use solar energy.

No abstract

This paper presents the results of a combined experimental and theoretical study of microstructure and thermal shock resistance of an aluminosilicate ceramic. Shock-induced crack growth is studied in sintered structures produced from powders with different particle size ranges. The underlying crack/microstructure interactions and toughening mechanisms are elucidated via scanning electron microscopy (SEM). The resulting crack-tip shielding levels (due to viscoelastic crack bridging) are estimated using fracture mechanics concepts. The implications of the work are discussed for the design of high refractory ceramics against thermal shock.