ABSTRACT:The choice of a superplasticiser (SP) for concrete is of great complexity, as it is well known that properties of the end product are related to admixture and its compatibility with concrete components. Very few studies have been conducted on the compatibility between SPs and the sand of mortars and concretes, however. Practical experience has shown that sand fineness and mineralogical composition affect water demand and admixture consumption. Clay-containing sand has been found also to adsorb SPs, reducing the amount available in solution for adsorption by the cement. This study analysed the isotherms for PCE and BNS superplasticiser adsorption on four sands with different fineness and compositions commonly used to prepare mortars and concretes. BNS-based SP did not adsorb on sands, while PCE-based admixtures exhibited variable adsorption depending on different factors. The adsorption curves obtained revealed that the higher the sand fineness, the finer the particle size distribution and the higher the clay material, the greater was PCE admixture adsorption/ consumption. RESUMEN: Adsorción de aditivos PCE y BNS en arenas con diferente composición y distribución de tamaño departículas. La elección de un superplastificante (SP) para el hormigón es un proceso complejo, ya que las propiedades del producto final se relacionan con la naturaleza del aditivo y su compatibilidad con los componentes del hormigón. Sin embargo hay pocos estudios sobre la compatibilidad entre los SPs y arenas utilizadas en morteros y hormigones. En la práctica se ha demostrado que la finura y la composición mineralógica de la arena afectan a la demanda de agua y al consumo de SPs. Las arcillas que pueden encontrarse en las arenas pueden también adsorber aditivos, reduciendo la cantidad disponible en solución para la adsorción por el cemento. Se han analizado las isotermas de adsorción para SPs de tipo PCE y BNS en cuatro arenas de diferente finura y composicion comúnmente utilizado para preparar morteros y hormigones. El aditivo BNS no se adsorbe en las arenas, mientras que los PCE mostraron adsorción variable. Las curvas de adsorción revelaron que cuanto mayor es la finura de arena, menor la distribución del tamaño de partícula y mayor el contenido de arcilla mayor era adsorción/intercalación de aditivos PCE en las arenas.

7Ba ions are known to immobilise sulfates by forming BaSO 4 . The use of witherite 8 (BaCO 3 ) as a full or partial substitute for gypsum to regulate C 3 A (3CaO•Al 2 O 3 ) 9 hydration was consequently studied with a view to establishing its correct dosage in 10 sulfate-resistant cements presently under development. 11 12The hydration rate of synthetic C 3 A was determined in the presence of varying 13 percentages of gypsum, witherite, and gypsum+witherite by running conduction 14 calorimetry analyses on early age (20-h) samples. The hydration products were 15 subsequently identified with XRD, FTIR and DTA/TG. 16 17The addition of (20-42wt%) witherite to C 3 A neither regulated the speedy reaction of 18 the latter with water nor reacted with the aluminate. Gypsum+witherite blends proved 19 able to regulate C 3 A hydration. The heat flow curves for all the samples studied 20 exhibited an induction period, an indication that gypsum acted as a C 3 A hydration 21 regulator while at the same time reacting with witherite to form barite. 22 23

RESUMENEl objetivo de este trabajo es profundizar en el conocimiento del comportamiento reologico de morteros de cementos activados alcalinamente (Alkali-Activated Materials, AAMs), determinando el efecto del diámetro máximo del árido y su naturaleza (silíceo, calizo y árido reciclado). Morteros de OPC se utilizan de referencia. Se realizaron ensayos de fluidez y de Stress Growth Test; también se determinaron los parámetros reológicos por el ensayo de curva de flujo. Los morteros de AAMs son más sensible que los de OPC a la variación del diámetro máximo de los áridos; aunque no se han observado diferentes comportamientos asociados a la naturaleza del mismo. Se ha demostrado que todos los morteros se ajustan al modelo reológico de Bingham, independientemente del diámetro máximo de los áridos y de la naturaleza de los mismos.PALABRAS CLAVE: comportamiento reologico, diámetro máximo de árido, morteros, geopolímeros, áridos reciclados. 1.-INTRODUCCIÓNSon muchos los estudios realizados sobre los factores que afectan a la reología y trabajabilidad de los morteros de cemento portland (OPC), entre ellos destacan: el contenido de agua, la relación árido/ligante, el tamaño, la forma y naturaleza del árido, la adición de aditivos, etc. Banfill [1] observó que al aumentar el contenido de agua, manteniendo constantes las proporciones de los otros constituyentes, disminuía el esfuerzo umbral de cizalla y la viscosidad. Por otra parte, la disminución del tamaño máximo del árido requiere aumentar el contenido de agua en la mezcla, y además, el aumento de la finura del árido, generalmente, conduce a incrementos en esfuerzo umbral de cizalla y en la viscosidad [2][3][4]. Los morteros con árido triturado presentan un mayor esfuerzo umbral de cizalla y una mayor viscosidad plástica que los morteros con áridos con morfologías redondeadas [4]. La reutilización de árido procedente de residuos de construcción supone un paso más para la eco-eficiencia y su influencia en el comportamiento mecánico y 55