This report demonstrates the fi rst pH-dependent synthesis of pepsinmediated gold nanoclusters (AuNCs) with blue-, green-, and red-fl uorescent emission from Au 5 (Au 8 ), Au 13 , and Au 25 , respectively. Pepsin is a gastric aspartic proteinase (molecular weight, 34 550 g/mol) that plays an integral role in the digestive process of vertebrates. It was found that the pH of the reaction solution was critical in determining the size of Au NCs (i.e., the number of gold atoms of AuNCs). Interestingly, enzyme function of pepsin contributes to the formation of these AuNCs. The photo-stability of the Au 25 (or Au 13 ) NCs is much higher than that of Au 5 NCs (i.e., Au 25 ∼ Au 13 > > Au 5 ). The pepsin-mediated Au 25 NCs were also found to be useful as fl uorescent sensors for the detection of Pb 2 + ions by enhanced fl uorescence and the detection of Hg 2 + ions by fl uorescence quenching. Although the detailed formation mechanisms of these AuNCs require further analysis, the synthetic route using proteinase demonstrated here is promising for preparing new types of fl uorescent metal nanoclusters for application in catalysis, optics, biological labeling, and sensing.

The decomposition of persistent and bioaccumulative perfluorooctanoic acid (PFOA) in water by UV-visible light irradiation, by H202 with UV-visible light irradiation, and by a tungstic heteropolyacid photocatalyst was examined to develop a technique to counteract stationary sources of PFOA. Direct photolysis proceeded slowly to produce CO2, F-, and short-chain perfluorocarboxylic acids. Compared to the direct photolysis, H2O2 was less effective in PFOA decomposition. On the other hand, the heteropolyacid photocatalyst led to efficient PFOA decomposition and the production of F- ions and CO2. The photocatalyst also suppressed the accumulation of short-chain perfluorocarboxylic acids in the reaction solution. PFOA in the concentrations of 0.34-3.35 mM, typical of those in wastewaters after an emulsifying process in fluoropolymer manufacture, was completely decomposed by the catalyst within 24 h of irradiation from a 200-W xenon-mercury lamp, with no accompanying catalyst degradation, permitting the catalyst to be reused in consecutive runs. Gas chromatography/mass spectrometry (GC/MS) measurements showed no trace of environmentally undesirable species such as CF4, which has a very high global-warming potential. When the (initial PFOA)/(initial catalyst) molar ratio was 10: 1, the turnover number for PFOA decomposition reached 4.33 over 24 h of irradiation.

Photochemical decomposition of persistent perfluorocarboxylic acids (PFCAs) in water by use of persulfate ion (S2O8(2-)) was examined to develop a technique to neutralize stationary sources of PFCAs. Photolysis of S2O8(2-) produced highly oxidative sulfate radical anions (SO4-), which efficiently decomposed perfluorooctanoic acid (PFOA) and other PFCAs bearing C4-C8 perfluoroalkyl groups. The major products were F- and CO2; also, small amounts of PFCAs with shorter than initial chain lengths were detected in the reaction solution. PFOA at a concentration of 1.35 mM (typical of that in untreated wastewater after an emulsifying process in fluoropolymer manufacture) was completely decomposed by a photochemical system with 50 mM S2O8(2-) and 4 h of irradiation from a 200-W xenon-mercury lamp. The initial PFOA decomposition rate was 11 times higherthan with photolysis alone. All sulfur-containing species in the reaction solution were eventually transformed to sulfate ions by this method. This method was successfully applied to the decomposition of perfluorononanoic acid contained in a floor wax solution.

No abstract

In this study, we investigated the catalytic properties of N,N-dimethylformamide (DMF)-stabilized gold nanoclusters (AuNCs) in the reduction of 4-nitrophenol (PNP) to 4-aminophenol by NaBH(4), a well known model reaction to be catalyzed by metal surfaces. The DMF-stabilized AuNCs were prepared in DMF by a surfactant-free method. The DMF-stabilized AuNCs showed high catalytic activity even when used in small quantities (∼10(-7) g). The pseudo-first-order rate constant (k(app)) and activation energy were estimated to be 3 × 10(-3) s(-1) and 31 kJ mol(-1), respectively, with 1.0 μM of the gold catalyst at 298 K. The catalytic activity of the DMF-stabilized AuNCs was strongly influenced by the layer of adsorbed DMF on the Au NCs. This layer of adsorbed DMF prohibited the reactants from penetrating to the surface of the AuNCs via the diffusion at the beginning of the reaction, resulting in an induction time (t(0)) before PNP reduction began. Restructuring of the DMF layer (essentially a form of activation) was the key to achieving high catalytic activity. In addition, atomically monodisperse Au(25)(SG)(18)NCs (SG: glutathione) showed higher catalytic activity in the PNP reduction (k(app) = 8 × 10(-3) s(-1)) even with a low catalyst concentration (1.0 μM), and there was no induction time (t(0)) in spite of the strongly binding ligand glutathione. This suggested that the catalytically active surface sites of the Au(25)(SG)(18)NCs were not sterically hindered, possibly because of the unique core-shell-like structure of the NCs. Retaining these open sites on AuNCs may be the key to making the NCs effective catalysts.

No-template synthesis of surface clean platinum nanomaterials with thin projections (petals) on the Pt nanoparticle surface, termed Pt nanoflowers, has been developed, and Pt nanoflowers have achieved superior performance on surface-assisted laser desorption/ionization mass spectrometry (SALDI−MS) of biomolecules. With this new material, one can obtain high-resolution mass spectra with lower laser energy and smaller sample amounts, and no organic matrix is needed for laser desorption/ionization. The mass spectra also have fewer obstacle peaks at the lower m/z region. Furthermore, this novel substrate is quite stable against aging and showed no sweet-spot problems, that is, equal sensitivity on the whole substrate surface. Various biomolecules, including peptides and phospholipids, were examined, and Pt nanoflowers showed good performance for matrix-free laser desorption/ionization MS of these materials.

Decomposition of perfluorooctanesulfonate (PFOS) and related chemicals in subcritical water was investigated. Although PFOS demonstrated little reactivity in pure subcritical water, addition of zerovalent metals to the reaction system enhanced the PFOS decomposition to form F-ions, with an increasing order of activity of no metal approximately equal Al < Cu < Zn << Fe. Use of iron led to the most efficient PFOS decomposition: When iron powder was added to an aqueous solution of PFOS (93-372 microM) and the mixture was heated at 350 degrees C for 6 h, PFOS concentration in the reaction solution fell below 2.2 microM (detection limit of HPLC with conductometric detection), with formation of F-ions with yields [i.e., (moles of F- formed)/(moles of fluorine content in initial PFOS) x 100] of 46.2-51.4% and without any formation of perfluorocarboxylic acids. A small amount of CHF3 was detected in the gas phase with a yield [i.e., (moles of CHF3)/(moles of carbon content in initial PFOS) x 100] of 0.7%, after the reaction of PFOS (372 microM) with iron at 350 degree C for 6 h. Spectroscopic measurements indicated that PFOS in water markedly adsorbed on the iron surface even at room temperature, and the adsorbed fluorinated species on the iron surface decomposed with rising temperature, with prominent release of F- ions to the solution phase above 250 degrees C. This method was also effective in decomposing other perfluoroalkylsulfonates bearing shorter chain (C2-C6) perfluoroalkyl groups and was successfully applied to the decomposition of PFOS contained in an antireflective coating agent used in semiconductor manufacturing.

No abstract