BackgroundSelective laser melting (SLM) titanium is an ideal option to manufacture customized implants with suitable surface modification to improve its bioactivity. The peri-implant soft tissues form a protective tissue barrier for the underlying osseointegration. Therefore, original microrough SLM surfaces should be treated for favorable attachment of surrounding soft tissues.Material and methodsIn this study, anodic oxidation (AO) was applied on the microrough SLM titanium substrate to form TiO2 nanotube arrays. After that, calcium phosphate (CaP) nanoparticles were embedded into the nanotubes or the interval of nanotubes by electrochemical deposition (AOC). These two samples were compared to untreated (SLM) samples and accepted mechanically polished (MP) SLM titanium samples. Scanning electron microscopy, energy dispersive spectrometry, X-ray diffraction, surface roughness, and water contact angle measurements were used for surface characterization. The primary human gingival epithelial cells (HGECs) and human gingival fibroblasts (HGFs) were cultured for cell assays to determine adhesion, proliferation, and adhesion-related gene expressions.ResultsFor HGECs, AOC samples showed significantly higher adhesion, proliferation, and adhesion-related gene expressions than AO and SLM samples (P<0.05) and similar exceptional ability in above aspects to MP samples. At the same time, AOC samples showed the highest adhesion, proliferation, and adhesion-related gene expressions for HGFs (P<0.05).ConclusionBy comparison between each sample, we could confirm that both anodic oxidation and CaP nanoparticles had improved bioactivity, and their combined utilization may likely be superior to mechanical polishing, which is most commonly used and widely accepted. Our results indicated that creating appropriate micro-/nano-topographies can be an effective method to affect cell behavior and increase the stability of the peri-implant mucosal barrier on SLM titanium surfaces, which contributes to its application in dental and other biomedical implants.

No abstract

Fast ion conduction and stable interfaces are predicted to be important in the development of new electrolytes. However, many unconventional solvents for electrolytes remain challenging, although they are fast ion...

Selective laser melting (SLM) has promising prospects in manufacturing customized implants, however the rough surface of SLM titanium specimen can facilitate bacterial adherence and biofilm formation, which is a risk to implant success. Therefore, surface modification is required to enhance its antibacterial efficacy. Sandblasting, anodization and electrochemical deposition were applied to construct a novel composite nanostructure of nanophase calcium phosphate embedded to TiO2 nanotubes on microrough SLM titanium substrates (NTN). NTN samples were compared with TiO2 nanotubes (NT) samples, mechanical polished (MP) samples and untreated SLM titanium samples. Surface characterization were analyzed using scanning electron microscope, energy dispersive spectroscopy, x-ray photoelectron spectroscopy, x-ray diffraction, a three dimensional profilometer and a contact angle measuring device. Bacteria adhesion assay for bacteria colony counting and bacteria LIVE/DEAD staining was conducted using Streptococcus mutans and Streptococcus sanguinis. Both S. mutans and S. sanguinis adherence on SLM samples were significantly higher than on NTN, NT and MP samples. The antibacterial efficacy of NTN samples was superior compared to NT and had no significant difference with MP samples, despite the fact that NTN samples had much rougher surface than MP samples. This study elucidates an efficient method to enhance antibacterial efficacy on rough SLM surfaces, which contributes to its application in dental and other biomedical implants.

Background Micro/nano-textured hierarchical titanium topography is more bioactive and biomimetic than smooth, micro-textured or nano-textured titanium topographies. Bone marrow mesenchymal stem cells (BMSCs) and exosomes derived from BMSCs play important roles in the osseointegration of titanium implants, but the effects and mechanisms of titanium topography on BMSCs-derived exosome secretion are still unclear. This study determined whether the secretion behavior of exosomes derived from BMSCs is differently affected by different titanium topographies both in vitro and in vivo. Results We found that both micro/nanonet-textured hierarchical titanium topography and micro/nanotube-textured hierarchical titanium topography showed favorable roughness and hydrophilicity. These two micro/nano-textured hierarchical titanium topographies enhanced the spreading areas of BMSCs on the titanium surface with stronger promotion of BMSCs proliferation in vitro. Compared to micro-textured titanium topography, micro/nano-textured hierarchical titanium topography significantly enhanced osseointegration in vivo and promoted BMSCs to synthesize and transport exosomes and then release these exosomes into the extracellular environment both in vitro and in vivo. Moreover, micro/nanonet-textured hierarchical titanium topography promoted exosome secretion by upregulating RAB27B and SMPD3 gene expression and micro/nanotube-textured hierarchical titanium topography promoted exosome secretion due to the strongest enhancement in cell proliferation. Conclusions These findings provide evidence that micro/nano-textured hierarchical titanium topography promotes exosome biogenesis and extracellular secretion for enhanced osseointegration. Our findings also highlight that the optimized titanium topography can increase exosome secretion from BMSCs, which may promote osseointegration of titanium implants.

Extra-short implants, of which clinical outcomes remain controversial, are becoming a potential option rather than long implants with bone augmentation in atrophic partially or totally edentulous jaws. The aim of this study was to compare the clinical outcomes and complications between extra-short implants (≤ 6 mm) and longer implants (≥ 8 mm), with and without bone augmentation procedures. Electronic (via PubMed, Web of Science, EMBASE, Cochrane Library) and manual searches were performed for articles published prior to November 2020. Only randomized controlled trials (RCTs) comparing extra-short implants and longer implants in the same study reporting survival rate with an observation period at least 1 year were selected. Data extraction and methodological quality (AMSTAR-2) was assessed by 2 authors independently. A quantitative meta-analysis was performed to compare the survival rate, marginal bone loss (MBL), biological and prosthesis complication rate. Risk of bias was assessed with the Cochrane risk of bias tool 2 and the quality of evidence was determined with the Grading of Recommendations Assessment, Development, and Evaluation (GRADE) approach. 21 RCTs were included, among which two were prior registered and 14 adhered to the CONSORT statement. No significant difference was found in the survival rate between extra-short and longer implant at 1- and 3-years follow-up (RR: 1.002, CI 0.981 to 1.024, P = 0.856 at 1 year; RR: 0.996, CI 0.968 to 1.025, P  = 0.772 at 3 years, moderate quality), while longer implants had significantly higher survival rate than extra-short implants (RR: 0.970, CI 0.944 to 0.997, P < 0.05) at 5 years. Interestingly, no significant difference was observed when bone augmentations were performed at 5 years (RR: 0.977, CI 0.945 to 1.010, P = 0.171 for reconstructed bone; RR: 0.955, CI 0.912 to 0.999, P < 0.05 for native bone). Both the MBL (from implant placement) (WMD: − 0.22, CI − 0.277 to − 0.164, P < 0.01, low quality) and biological complications rate (RR: 0.321, CI 0.243 to 0.422, P < 0.01, moderate quality) preferred extra-short implants. However, there was no significant difference in terms of MBL (from prosthesis restoration) (WMD: 0.016, CI − 0.036 to 0.068, P = 0.555, moderate quality) or prosthesis complications rate (RR: 1.308, CI 0.893 to 1.915, P = 0.168, moderate quality). The placement of extra-short implants could be an acceptable alternative to longer implants in atrophic posterior arch. Further high-quality RCTs with a long follow-up period are required to corroborate the present outcomes.Registration number The review protocol was registered with PROSPERO (CRD42020155342).

No abstract

Implant surface topography has been proven to determine the fate of adhered macrophage polarization, which is closely related to the cytoskeletal arrangement during adhesion. Our purpose was to establish a...