Abstract:MnAl is a promising rare-earth free permanent magnet for technological use. We have examined the effects of consolidation by back-pressure, assisted equal channel angular extrusion processing on mechanically-milled, gas-atomized Mn-46% at. Al powder. X-ray diffraction showed both that the extruded rod consisted mostly of metastable τ phase, with some of the equilibrium γ 2 and β phases, and that it largely retained the as-milled nanostructure. Magnetic measurements show a coercivity of ≤4.4 kOe and a magnetization at 10 kOe of ≤40 emu/g. In addition, extrusions exhibit greater than 95% of the theoretical density. This study opens a new window in the area of bulk MnAl magnets with improved magnetic properties for technological use.
MnAl alloys are very promising rare-earth-free permanent magnets. Nanocrystalline microstructures can have beneficial effects on the properties of magnetic MnAl alloys. In the present work we examined multiple routes to process MnAl alloys and studied the effects of milling on Mn-46 at.% Al powders. Mn54Al46 was produced via gas atomization, melt spinning, and rapid solidification rate processing. It was then mechanically milled using a water-cooled Union Process attritor for times up to 20 h. X-ray diffraction patterns showed the presence of mostly the high-temperature ε-phase with significant amounts of the equilibrium γ2 and β phases in both the cast and milled particulates. The powders were annealed for various temperatures and times in order to obtain the ferromagnetic τ-phase. Magnetic measurements of the optimally annealed powders showed a coercivity of 3.62 kOe and saturation magnetization of 59.8 emu g(-1) for mechanically milled gas-atomized powder annealed at 500 °C for 30 min.
Magnetic nanoparticle hyperthermia uses magnetically-induced heat to kill cancer cells. In an alternating magnetic field, the induced heat depends strongly on particles’ absorption properties. In order to achieve and maintain therapeutic temperatures inside a tumor and to minimize damage to normal tissues due to induced eddy currents, there is a need to develop new magnetic nanoparticles with improved heating characteristics. This paper investigates the magnetic heating properties of composite iron-cobalt ferrite nanoparticles CoxFeII1−xFeIII2O4 with 0≤x≤1. These composite materials are synthesized using a precipitation method. First, the Fe-Co nanoparticle synthesis is described, then their structure, size, magnetic and heating properties are measured and analyzed. The resulting nanoparticles were treated at temperatures 100–600°C in order to study any structural transformations and changes of physical properties. Finally, an empirical model is used to calculate both the nanoparticles’ coercivity and their specific absorption rates for different Co concentrations.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.