We demonstrated here a novel and facile synthesis of two-dimensional (2D) covalent organic thin film with pore size around 1.5 nm using a planar, amphiphilic and substituted heptacyclic truxene based triamine and a simple dialdehyde as building blocks by dynamic imine bond formation at the air/water interface using Langmuir-Blodgett (LB) method. Optical microscopy (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and atomic force microscopy (AFM), all unanimously showed the formation of large, molecularly thin and free-standing membrane that can be easily transferred on different substrate surfaces. The 2D membrane supported on a porous polysulfone showed a rejection rate of 64 and 71% for NaCl and MgSO, respectively, and a clear molecular sieving at molecular size around 1.3 nm, which demonstrated a great potential in the application of pretreatment of seawater desalination and separation of organic molecules.
Lithium-sulfur batteries suffer from severe self-discharge due to polysulfide dissolution into electrolytes. In this work, a chemically anchored polymer-coated (CAPC) sulfur electrode was prepared, through chemical bonding by coordinated Cu ions and cross-linking, to improve cyclability for Li/S batteries. This electrode retained specific capacities greater than 665 mAh g(-1) at high current density of 3.35 A g(-1) (2C rate) after 100 cycles with an excellent Coulombic efficiency of 100%.
The predominant method to prepare polymer membranes is based on phase inversion. However, this method always leads to a dense skin with low porosity when normal polymers are used. Using the self-assembly of certain block copolymers, it is possible to prepare uniform pores with high porosity, but the prices of these polymers are too high to be afforded in practical applications. Here, we report a novel strategy to prepare highly porous and asymmetric polymer membranes using the widely used poly(vinylidene fluoride) (PVDF) as a prototype. The method combines spinodal decomposition with phase inversion utilizing mixed solvents that have the unique upper critical solution temperature phase behavior. The spinodal decomposition generates a thin surface layer containing a high density of relatively uniform pores in the mesoporous range, and the phase inversion generates a thick bulk layer composed of macrovoids; the two types of structures are interconnected, yielding a highly permeable, selective, and mechanically strong porous membrane. The membranes show an order of magnitude higher water permeance than commercial membranes and efficient molecular sieving of macromolecules. Notably, our strategy provides a general toolbox to prepare highly porous membranes from normal polymers. By blending PVDF with cellulose acetate (CA), a highly porous PVDF/CA membrane was prepared and showed similarly high separation performance, but the higher hydrophilicity of CA improved the membrane flux in the presence of proteins.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.