Rheological and morphological studies were performed on polymer blends of ethylene-octene copolymer [polyethylene elastomer (PEE)] and polypropylene (PP). The viscosities of PEE, PP, and PEE/PP blends were analyzed using an Instron capillary rheometer and a Rheometrics Dynamic Stress Rheometer, SR 200. A non-Newtonian flow behavior was observed in all samples in the shear rate range from 27 to 2700 s Ϫ1 , whereas at shear rates in the range from 0.01 to 0.04 s Ϫ1 , a Newtonian flow behavior was verified. The scanning electron micrographs showed that dual-phase continuity may occur between 50 and 60 (wt %) of PEE. This result is consistent with the Sperling's model. The mechanical analysis showed that PEE/PP, with 5 wt % of PEE, presented an increase on the mechanical properties and as the PEE content increased, a negative deviation in relation to an empirical equation was observed. Thermal analysis showed that there were no change in the crystallization behavior of the matrix when different elastomer contents were added. Dynamic mechanical thermal analysis showed that samples with low PEE contents presented only one peak, indicating a certain degree of miscibility between the components of these blends.
Poly(D,L-lactide acid, PDLLA) has been researched for scaffolds in bone regeneration. However, its hydrophobocity and smooth surface impedes its interaction with biological fluid and cell adhesion. To alter the surface characteristics, different surface modification techniques have been developed to facilitate biological application. The present study compared two different routes to produce PDLLA/superhydrophilic vertically aligned carbon nanotubes:nanohydroxyapatite (PDLLA/VACNT-O:nHAp) scaffolds. For this, we used electrodeposition and immersion in simulated body fluid (SBF). Characterization by goniometry, scanning electron microscopy, X-ray diffraction, and infrared spectroscopy confirmed the polymer modifications, the in vitro bioactivity, and biomineralization. Differential scanning calorimetry and thermal gravimetric analyses showed that the inclusion of VACNT-O:nHA probably acts as a nucleating agent increasing the crystallization rate in the neat PDLLA without structural alteration. Our results showed the formation of a dense nHAp layer on all scaffolds after 14 days of immersion in SBF solution; the most intense carbonated nHAp peaks observed in the PDLLA/VACNT-O:nHAp samples suggest higher calcium precipitation compared to the PDLLA control. Both cell viability and alkaline phosphatase assays showed favorable results, because no cytotoxic effects were present and all produced scaffolds were able to induce detectable mineralization. Bone defects were used to evaluate the bone regeneration; the confocal Raman and histological results confirmed high potential for bone applications. In vivo study showed that the PDLLA/VACNT-O:nHAp scaffolds mimicked the immature bone and induced bone remodeling. These findings indicate surface improvement and the applicability of this new nanobiomaterial for bone regenerative medicine.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.