A method for the fabrication of interconnected ceramic sponges was used in the present work, designed by using a combination of two different, aqueous gel casting and sacrificial template, using aluminum nitride powder (99.97%) with a mean size of 2.4 micrometers. Two types of sponges were made by using two different monomers, acrylamide and methacrylamide, the resultants sponges have 60% of porosity after being sintered and pyrolyzed at temperature of 1673 K using an inert atmosphere of argon for 1 h. The hydrolysis evolution of this ceramic powder during the gelcasting process was studied by measuring the pH during the stirring time, the microstructure changes during the time of exposure were observed in a SEM. XRD were made to study the present phases after the gel was eliminated by thermal treatment at 873 K using an oxidizing atmosphere, observing a formation of up to 4 %wt. of cubic alumina phase which was made after the hydrolysis products. Infrared spectroscopy was used to study the changes in the ceramic powder.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.