The influence of continuous annealing variables on the microstructure and mechanical properties of a C-Mn Dual Phase (DP) steel was studied. The annealing cycles were simulated using a Gleeble machine. Some specimens were quenched at different stages of the annealing cycle in order to evaluate the microstructural evolution during the annealing process. Tensile tests and microstrutural analysis were carried out. The results showed that high heating rates increased the final recrystallization temperature and as a consequence the microstructure obtained was refined. Austenite grain nucleation and growth were also influenced by the heating rates. Soaking temperature was the most influent variable on the mechanical properties, i. e., the yield strength increased and the tensile strength decreased with an increase in the soaking temperature. Microstructural analysis showed that not only martensite, but also bainite and martensite-retained autenite constituent (MA) were formed. Undissolved carbides were also detected by transmission electron microscopy.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.