Melt electrospinning is widely used to manufacture fibers with diameters in the low micrometer range. Such fibers are suitable for many biomedical applications, including sutures, stents and tissue engineering. We investigated the preparation of polybutylene succinate microfibers using a single-nozzle laboratory-scale device, while varying the electric field strength, process throughput, nozzle-to-collector distance and the temperature of the polymer melt. The formation of a Taylor cone followed by continuous fiber deposition was observed for all process parameters, but whipping behavior was enhanced when the electric field strength was increased from 50 to 60 kV. The narrowest fibers (30.05 µm) were produced using the following parameters: electric field strength 60 kV, melt temperature 235 °C, throughput 0.1 mL/min and nozzle-to-collector distance 10 cm. Statistical analysis confirmed that the electric field strength was the most important parameter controlling the average fiber diameter. We therefore report the first production of melt-electrospun polybutylene succinate fibers in the low micrometer range using a laboratory-scale device. This offers an economical and environmentally sustainable alternative to conventional solution electrospinning for the preparation of safe fibers in the micrometer range suitable for biomedical applications.
Melt electrospinning is a polymer processing technology for the manufacture of microfibers and nanofibers. Additives are required to reduce the melt viscosity and increase its conductivity in order to minimize the fiber diameter, and can also impart additional beneficial properties. We investigated the preparation of polybutylene succinate (PBS) microfibers incorporating different weight percentages of two multifunctional additives (the organic dye curcumin and inorganic silver nanoparticles) using a single-nozzle laboratory-scale device. We determined the influence of these additives on the polymer melt viscosity, electrical conductivity, degradation profile, thermal behavior, fiber diameter, and antibacterial activity. The formation of a Taylor cone followed by continuous fiber deposition was observed for compounds containing up to 3% (w/w) silver nanoparticles and up to 10% (w/w) curcumin, the latter achieving the minimum average fiber diameter of 12.57 µm. Both additives reduced the viscosity and increased the electrical conductivity of the PBS melt, and also retained their specific antibacterial properties when compounded and spun into fibers. This is the first report describing the effect of curcumin and silver nanoparticles on the properties of PBS fibers manufactured using a single-nozzle melt-electrospinning device. Our results provide the basis to develop environmentally benign antibacterial melt-electrospun PBS fibers for biomedical applications.
Melt electrospinning is a simple, versatile, and widely used technique for the production of microfibers and sub-microfibers. Polybutylene succinate (PBS) is a promising raw material for the preparation of melt-electrospun fibers at the laboratory scale. The inclusion of additives in the PBS melt can reduce the final fiber diameter, but economically feasible larger-scale processes remain challenging. The fiber diameter can also be reduced by machine optimization, although this is expensive due to the complexity of melt-electrospinning devices. Changes in electrical field polarity have provided a low-cost strategy to reduce the diameter of fibers produced by solution-electrospinning, but there is little information about the effect of this parameter on the final diameter of melt-electrospun fibers. We therefore determined the effect of field polarity on the diameter of melt-electrospun PBS fibers at the laboratory scale and investigated the transferability of these results to our 600-nozzle pilot-scale device. Changing the polarity achieved a significant reduction in fiber diameter of ~50% at the laboratory scale and ~30% at the pilot scale, resulting in a minimum average fiber diameter of 10.88 µm. Although the effect of field polarity on fiber diameter was similar at both scales, the fibers in the web stuck together at the laboratory scale but not at the pilot scale. We have developed an inexpensive method to reduce the diameter of melt-electrospun PBS fibers and our data provide insight into the transferability of melt electrospinning from the laboratory to a pilot-scale machine.
Fibers with diameters in the lower micrometer range have unique properties suitable for applications in the textile and biomedical industries. Such fibers are usually produced by solution electrospinning, but this process is environmentally harmful because it requires the use of toxic solvents. Melt electrospinning is a sustainable alternative but the high viscosity and low electrical conductivity of molten polymers produce thicker fibers. Here, we used multifunctional biobased dyes as additives to improve the spinnability of polylactic acid (PLA), improving the spinnability by reducing the electrical resistance of the melt, and incorporating antibacterial activity against Staphylococcus aureus. Spinning trials using our 600-nozzle pilot-scale melt-electrospinning device showed that the addition of dyes produced narrower fibers in the resulting fiber web, with a minimum diameter of ~9 µm for the fiber containing 3% (w/w) of curcumin. The reduction in diameter was low at lower throughputs but more significant at higher throughputs, where the diameter reduced from 46 µm to approximately 23 µm. Although all three dyes showed antibacterial activity, only the PLA melt containing 5% (w/w) curcumin retained this property in the fiber web. Our results provide the basis for the development of environmentally friendly melt-electrospinning processes for the pilot-scale manufacturing of microfibers.
The color of textile fibers is typically imparted by submersion in a high-temperature dye bath. However, the treatment of the effluent is challenging and the textile industry is therefore a major source of water pollution. Current fashion trends favor biobased polymers such as polylactic acid (PLA) but exhaust dyeing at high temperatures causes hydrolytic degradation, reducing the crystallinity and tenacity of the yarn. To preserve the mechanical properties of PLA-based textiles, an alternative to exhaust dyeing called dope dyeing can be used, wherein colorants are incorporated into the polymer matrix during melt spinning. We evaluated this process by dope dyeing PLA with several colorants, then testing the thermal, physical, and mechanical properties of the yarn and the physical properties of circular-knitted fabrics. Although the colorants affected the crystallization behavior at lower cooling rates, during the melt-spinning process, the drawing speed had a greater effect on the crystallinity and mechanical properties of the dyed yarn. Scanning electron microscopy revealed that the colorants were well dispersed in the PLA matrix. We found that the colorants did not affect the physical properties of the knitted fabric. Our results can be used to develop more environmentally beneficial dope-dyed PLA yarn with improved mechanical properties.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.