In this work, the isothermal decomposition of poly(methyl methacrylate) synthesized in bulk by the radical route of methyl methacrylate in the presence of azobisisobutyronitrile as the initiator was carried out and monitored for the first time with the DART-Tof-MS technique at different temperatures. Nuclear magnetic resonance (NMR) analysis revealed a predominantly atactic microstructure, and size-exclusion chromatography (SEC) analysis indicated a number average molecular weight of 3 × 105 g·mol−1 and a polydispersity index of 2.47 for this polymer. Non-isothermal decomposition of this polymer carried out with thermogravimetry analysis (TGA) showed that the weight loss process occurs in two steps. The first one starts at approximately 224 °C and the second at 320 °C. The isothermal decomposition of this polymer carried out and monitored with the DART-Tof-MS method revealed only one stage of weight loss in this process, which begins at approximately 250 °C, not far from that of the second step observed in the case of the non-isothermal process conducted with the TGA method. The results obtained with the MS part of this technique revealed that the isothermal decomposition of this polymer regenerates a significant part of methyl methacrylate monomer, which increases with temperature. This process involves radical chain reactions leading to homolytic chain scissions and leading to the formation of secondary and tertiary alkyl radicals, mainly regenerating methyl methacrylate monomer through an unzipping rearrangement. Although they are in the minority, other fragments, such as the isomers of 2-methyl carboxyl, 4-methyl, penta-2,4-diene and dimethyl carbate, are also among the products detected. At 200 °C, no trace of monomer was observed, which coincides with the first step of the weight loss observed in the TGA. These compounds are different to those reported by other researchers using TGA coupled with mass spectrometry in which methyl isobutyrate, traces of methyl pyruvate and 2,3-butanonedione were detected.

A series of poly(vinyl acetate-co-2-hydroxyethylmethacrylate)/acyclovir drug carrier systems (HEMAVAC) containing different acyclovir contents was prepared through bulk free radical polymerization of 2-hydroxyethyl methacrylate with vinyl acetate (VAc) in presence of acyclovir (ACVR) as the drug using a LED lamp in presence of camphorquinone as the photoinitiator. The structure of the drug carrier system was confirmed by FTIR and 1HNMR analysis, and the uniform dispersion of the drug particles in the carrier was proved by DSC and XRD analysis. The study of the physico-chemical properties of the prepared materials, such as the transparency, swelling capacity, wettability and optical refraction, was carried out by UV–visible analysis, a swelling test and measurement of the contact angle and the refractive index, respectively. The elastic modulus and the yield strength of the wet prepared materials were examined by dynamic mechanical analysis. The cytotoxicity of the prepared materials and cell adhesion on these systems were studied by LDH assay and the MTT test, respectively. The results obtained were comparable to those of standard lenses with a transparency of 76.90–89.51%, a swelling capacity of 42.23–81.80% by weight, a wettability of 75.95–89.04 o, a refractive index of 1.4301–1.4526 and a modulus of elasticity of 0.67–1.50 MPa, depending on the ACVR content. It was also shown that these materials exhibit no significant cytotoxicity; on the other hand, they show significant cell adhesion. The in vitro dynamic release of ACVR in water revealed that the HEMAVAC drug carrier can consistently deliver uniformly adequate amounts of ACVR (5.04–36 wt%) over a long period (7 days) in two steps. It was also found that the solubility of ACVR obtained from the release process was improved by 1.4 times that obtained by direct solubility of the drug in powder form at the same temperature.