After long-term ageing, the structure of graphene oxide prepared by the modified Hummers method changed. Because of the desorption of oxygen-containing functional groups, the C/O ratio of graphene oxide increased from 1.96 to 2.76. However, the average interlayer distance decreased from 0.660 to 0.567 nm. The content of -CH- and -CH
2
- decreased; however, the type of oxygen-containing functional groups did not change. Moreover,
I
D
/
I
G
increased from 0.87 to 0.92, indicating that the defect density decreased because of desorbing oxygen functional groups after ageing. When the temperature exceeded 60°C, CO
2
produced by decomposing graphene oxide was detected. The thermal decomposition changed after ageing. The decomposition peak temperature decreased from 216°C to 195°C. The CO
2
amount produced remained almost unchanged; however, the amount of CO, SO
2
and H
2
O decreased. After ageing, the apparent activation energy of graphene oxide decreased from 150 to 134 kJ mol
−1
.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.