A simple and easier chemical method for preparing spongy gold nanocrystals has been developed on the basis of a modified-citrate reduction technique of the corresponding gold salt at 25 degrees C in the absence of template. These nanocrystals possessed autocatalytic behavior and exhibited pronounced catalytic activity in the borohydride reduction of 4-nitrophenol due to their unique spongy morphology.

Synthetic oligopeptides containing redox-active tyrosine residues have been employed to prepare gold and silver nanoparticles. In this reduction process an electron from the tyrosinate ion of the peptide is transferred to the metal ion at basic pH through the formation of a tyrosyl radical, which is eventually converted to its dityrosine form during the reaction. This reaction mechanism was confirmed from UV-visible, fluorescence, and EPR spectroscopy and was found to be pH-dependent. Transmission electron microscopy measurement shows that the average size and the monodispersity of gold nanoparticles increase as the number of tyrosine residues in the peptide increases. The kinetic study, based on spectrophotometric measurements of the surface plasmon resonance optical property, shows that the rate of formation of gold nanoparticles was much faster at higher pH than at lower pH and was also dependent on the number of tyrosine residues present in the peptide. The dityrosine form of the peptide was found to retain reducing properties like those of tyrosine in basic medium.

A novel gold nanoparticle-tripeptide (GNP-tripeptide) conjugate was prepared by peptide in-situ redox technique at ambient temperatureusing a newly designed tripeptide. This new tripeptide was nso designed that it has a C-terminus tyrosine residue, which reduced Au+3 to Au, and the terminally located free amino group was bound to the gold nanoparticle (GNP) surface resulting in highly stable Au colloids. The average diameter of the tripeptide-stabilized GNP is 8.7 +/- 2.3 nm. Tripeptide bound gold nanoparticles formed three-dimensional assemblies in the presence of an excess of similar or disimilar tripeptides. The aggregation of GNPs results in a red shift in the surface plasmon resonance from lambda max = 527 to 556 nm. The effect of the solvent, concentration, and nature of the tripeptides on the assembly process were investigated by TEM and UV-visible spectroscopy.

Conducting carbon quantum dots are reported, and single quantum dots were probed using spreading resistance imaging.

Thermoresponsive gold nanoparticles (GNPs) have been prepared by the borohydride reduction of gold salt in the presence of water-soluble polymer, poly(vinyl methyl ether) (PVME). The PVME-coated GNPs (PVME-GNPs) have been assembled into large aggregates in the presence of polyelectrolytes, viz., poly(sodium-4 styrene sulfonate) and sodium salt of carboxymethylcellulose at low pH by raising the solution temperature from 20 to 40 degrees C. Increase of temperature triggers the interparticle association due to hydrophobic interaction of pendent methyl group of the surface adsorbed PVME. This assembly process is reversible with respect to temperature and pH of the medium and was studied by monitoring the change in surface plasmon resonance band of PVME-GNPs. Three-dimensional assemblies of various architectures, depending on the concentration of polyelectrolytes, were observed through transmission electron microscopy. A mechanistic model has been suggested for the reversible assembly formation that suits well with the experimental observations. The changes in optical properties of the PVME-GNPs due to their aggregation/disaggregation enabled us to use it as an effective tool to monitor the change in lower critical solution temperature (LCST) of PVME in the presence of polyelectrolytes due to interpolymer complexation at low pH. This result agrees well with the variation of LCST of pure aqueous PVME solution in the presence of polyelectrolytes measured by conventional turbidimetric technique.