No abstract

Hexagonal wurtzite phased ZnO:Er3+/Yb3+ thin films with various Yb concentrations were deposited on Si(111) substrate by Aerosol Assisted Chemical Vapor Deposition process. Post-annealed films at 1000 °C in air atmosphere showed a crystallinity enhancement. Yb3+ (4F7/2 → 4F5/2) 1000 nm emission increased with the increase of Yb3+ concentration emanating from an Er-Yb energy transfer. The reflectance percentage of 12% was achieved in the [250–1000 nm] range, and the refractive index of 1.97 was obtained for 632 nm wavelength. These results suggest that the (3 mol. % Er, 9 mol. % Yb) codoped film is a highly efficient antireflective downconversion layer for enhancing Si solar cell efficiency.

No abstract

International audienceErbium-doped yttrium oxide films are prepared from yttrium acetylacetonate (Y(C(5)H(7)O2)(3)) and erbium (III) tris(2,2,6,6-tetramethyl-3,5-heptanedionate) (Er(TMHD)(3)) under standard conditions by UV-aerosol-assisted metal-organic (AA-MOCVD), using air with controlled humidity as the carrier gas. The structure and deposition rate are optimized by studying three experimental parameters; substrate temperature, relative humidity (RH) of the carrier gas, and UV-assistance. Taking all these parameter effects under consideration, the maximum deposition rates are reached under low humidity air and with UV-assistance. Nevertheless, as-deposited Er:Y(2)O(3) films crystallize in the Y(2)O(3) cubic structure and present a very low organic contamination when depositions take place under high air humidity and with UV-assistance. The refractive index of yttrium oxide films under these conditions are relatively high, reaching 1.86 when deposited at 410 degrees C

No abstract

A new NYVO:Eu3+ phosphor was prepared using the sol–gel method and its exhibits high-brightness and thermally stable emission that could be used for display and temperature sensing applications.

No abstract

No abstract