Cu2ZnSnS4(CZTS) absorber layers grown by sputtering were investigated by photoluminescence before and after the chemical bath deposition of CdS in order to evaluate the possible passivation of point defects by Cd atoms at the absorber/buffer layer interface. According to the literature, a broad emission around 1.21 eV was observed at low temperature under above bandgap excitation of the as-grown CZTS samples. Broad bands at 1.075 eV and 0.85 eV were detected for the first time under below bandgap excitation of the as-grown CZTS samples at low temperature, which were explained in terms of radiative transitions involving point defect-related levels determined in the literature by first-principles calculations. The emissions observed in the as-grown samples were monitored by both above and below bandgap excitations also in standard CZTS solar cells produced on the same layers. The obtained results suggest that, as in the case of Cu(In, Ga)Se2, Cd atoms passivate point defects at the absorber/buffer layer interface also in CZTS.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.