The commonly used electron transport material (6,6)-phenyl-C61 butyric acid methyl ester (PCBM) for perovskite solar cells (PSC) with inverted planar structures suffers from properties such as poor film-forming. In this manuscript, we demonstrate a simple method to improve the film-forming properties of PCBM by doping PCBM with poly(9,9-dioctylfluorene-co-benzothiadiazole) (F8BT) as the electron transport layer (ETL), which effectively enhances the performance of CH3NH3PbI3 based solar cells. With 5 wt % F8BT in PCBM, the short circuit current (JSC) and fill factor (FF) of PSC both significantly increased from 17.21 ± 0.15 mA·cm−2 and 71.1 ± 0.07% to 19.28 ± 0.22 mA·cm−2 and 74.7 ± 0.21%, respectively, which led to a power conversion efficiency (PCE) improvement from 12.6 ± 0.24% to 15 ± 0.26%. The morphology investigation suggested that doping with F8BT facilitated the formation of a smooth and uniform ETL, which was favorable for the separation of electron-hole pairs, and therefore, an improved performance of PSC.
A π-conjugated small molecule N, N’-bis(naphthalen-1-yl)-N, N’-bis(phenyl)benzidine (NPB) was introduced into poly(9-vinylcarbazole) (PVK) as a hole transport layer (HTL) in inverted perovskite solar cells (PSCs). The NPB doping induces a better perovskite crystal growth, resulting in perovskite with a larger grain size and less defect density. Thus, the VOC, JSC, and FF of the PSC were all enhanced. Experimental results show that it can be ascribed to the reduction of surface roughness and improved hydrophilicity of the HTL. The effect of NPB on the aggregation of PVK was also discussed. This work demonstrates the great potential of PVK as the HTL of PSCs and provides an attractive alternative for HTL to realize high-efficiency PSCs.
Efficient polymer white-light-emitting diodes (WPLEDs) with an active polymer layer have been demonstrated. The white emission consists of two emission bands in the blue and yellow ranges. The blue polymer is a host (PFO) and the yellow dopant is a phosphorescent dye of Ir(CzBPPF) 2 (PZ), i.e. Iridium(III) bis(2,4-diflurophenyl-2-pyridine-4-phenyl-p-carbarzole)(2-(4H-1,2,4-triazol-3-yl)-pyridine). When the doping concentration of Ir(CzBPPF) 2 (PZ) is 2 wt%, pure white light is obtained, which possesses stable white light CIE coordinates, efficiency of 5.6 cd A −1 (9.5 V) and luminance of 7656 cd m −2 (14 V). The EL process in the device was proved mainly to be the charge trap mechanism.
Nonradiative recombination losses caused by defects in the perovskite layer seriously affects the efficiency and stability of perovskite solar cells (PSCs). Hence, defect passivation is an effective way to improve the performance of PSCs. In this work, trichloromelamine (TCM) was used as a defects passivator by adding it into the perovskite precursor solution. The experimental results show that the power conversion efficiency (PCE) of PSC increased from 18.87 to 20.15% after the addition of TCM. What’s more, the environmental stability of PSCs was also improved. The working mechanism of TCM was thoroughly investigated, which can be ascribed to the interaction between the –NH– group and uncoordinated lead ions in the perovskite. This work provides a promising strategy for achieving highly efficient and stable PSCs.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.