Ferroelectric HfO2-based thin films, which can exhibit ferroelectric properties down to sub-10 nm thicknesses, are a promising candidate for emerging high density memory technologies. As the ferroelectric thickness continues to shrink, the electrode-ferroelectric interface properties play an increasingly important role. We investigate the TaN interface properties on 10 nm thick Si-doped HfO2 thin films fabricated in a TaN metal-ferroelectric-metal stack which exhibit highly asymmetric ferroelectric characteristics. To understand the asymmetric behavior of the ferroelectric characteristics of the Si-doped HfO2 thin films, the chemical interface properties of sputtered TaN bottom and top electrodes are probed with x-ray photoelectron spectroscopy. Ta-O bonds at the bottom electrode interface and a significant presence of Hf-N bonds at both electrode interfaces are identified. It is shown that the chemical heterogeneity of the bottom and top electrode interfaces gives rise to an internal electric field, which causes the as-grown ferroelectric domains to preferentially polarize to screen positively charged oxygen vacancies aggregated at the oxidized bottom electrode interface. Electric field cycling is shown to reduce the internal electric field with a concomitant increase in remanent polarization and decrease in relative permittivity. Through an analysis of pulsed transient switching currents, back-switching is observed in Si-doped HfO2 thin films with pinched hysteresis loops and is shown to be influenced by the internal electric field.

No abstract

Ferroelectric HfO2 is an attractive candidate for future ferroelectric random access memory devices due to its compatibility with the complementary metal-oxide-semiconductor process, conformal deposition, and scaling ability. Crystallization of HfO2 with different dopants and annealing conditions can produce the stabilization of the monoclinic, tetragonal, cubic, or orthorhombic crystal phases. In this work, the authors observe ferroelectric behavior in Si-doped hafnium oxide with TiN and Ir electrodes. Atomic layer deposited 10 nm HfO2 capacitors doped with varying concentrations of SiO2 have been fabricated in the metal–ferroelectric–insulator–semiconductor (MFIS) structure. The ferroelectric characteristics of thin film HfO2 are compared in the MFIS and metal–ferroelectric–metal configurations. Post-metallization anneals were applied to all thin film ferroelectric HfO2 capacitors, resulting in a remanent polarization of up to 22 μC/cm2 and a range of observed coercive voltages, emphasizing the importance of the annealing conditions, electrode materials, and device structure on the ferroelectric properties of thin film HfO2.

No abstract

Ferroelectric HfO2 thin films 10 nm thick are simultaneously doped with Al and Si. The arrangement of the Al and Si dopant layers within the HfO2 greatly influences the resulting ferroelectric properties of the polycrystalline thin films. Optimizing the order of the Si and Al dopant layers led to a remanent polarization of ∼20 μC/cm2 and a coercive field strength of ∼1.2 MV/cm. Post-metallization anneal temperatures from 700 °C to 900 °C were used to crystallize the Al and Si doped HfO2 thin films. Grazing incidence x-ray diffraction detected differences in peak broadening between the mixed Al and Si doped HfO2 thin films, indicating that strain may influence the formation of the ferroelectric phase with variations in the dopant layering. Endurance characteristics show that the mixed Al and Si doped HfO2 thin films exhibit a remanent polarization greater than 15 μC/cm2 up to 108 cycles.

Atomic layer deposited Si-doped HfO2 thin films approximately 10 nm thick are deposited with various Si-dopant concentrations and distributions. The ferroelectric behavior of the HfO2 thin films are shown to be dependent on both the Si mol. % and the distribution of Si-dopants. Metal-ferroelectric-insulator-semiconductor capacitors are shown to exhibit a tunable remanent polarization through the adjustment of the Si-dopant distribution at a constant Si concentration. Inhomogeneous layering of Si-dopants within the thin films effectively lowers the remanent polarization. A pinched hysteresis loop is observed for higher Si-dopant concentrations and found to be dependent on the Si layering distribution.

No abstract

Understanding the relation between the surface composition of a catalyst and its catalytic activity toward species is key to enhancing the science of catalysis. The current state of knowledge on platinum-ruthenium (Pt-Ru) activity toward methanol is that an alloy with a 1:1 ratio of the two metals exhibits the highest activity. Here, we correlate the activity of a bilayer Pt-Ru catalyst to its surface composition. By using electrochemical techniques such as Cyclic Voltammetry (CV) and Copper Underpotential Deposition (Cu-UPD) in conjunction with Kelvin Probe Force Microscopy (KPFM), we demonstrate the effect of surface Fermi energy on catalyst activity.