Graft copolymerization of styrene onto deproteinized natural rubber (DPNR) using tert-butyl hydroperoxide (TBHPO) and tetraethylene pentamine (TEPA) as redox initiator have been investigated. The effects of initiator and monomer concentration on conversion and grafting efficiency were studied. The dynamic mechanical and thermal properties of the graft copolymer were investigated over the wide range of temperatures. It is shown that a high value of storage modulus for the graft copolymer, which was about 25 times as high as that of DPNR, was achieved. The graft copolymer (DPNR-graft-PS) showed the outstanding tensile strength and stable thermal properties. These enhancements were attributed to the interaction between NR and polystyrene as a result of the graft copolymerization. Morphology observation by transmission electron micrograph (TEM) revealed that the core-shell arrangement of the DPNR-graft-PS with about 30 nm in thickness of polystyrene nano-layer was achieved.

Reaction after mixing of liquid epoxidized natural rubber/poly(L-lactide) blend was performed to enhance the compatibility of the blend. The liquid epoxidized natural rubber was prepared by epoxidation of deproteinized natural rubber with peracetic acid in latex stage followed by depolymerization with peroxide and propanal. The resulting liquid deproteinized natural rubber having epoxy group (LEDPNR) was mixed with poly(L-lactide) (PLLA) to investigate the compatibility of the blend through differential scanning calorimetry, optical light microscopy, and NMR spectroscopy. After heating the blend at 473 K for 20 min, glass transition temperature (T g ) of LEDPNR in LEDPNR/PLLA blend increased from 251 to 259 K, while T g and melting temperature (T m ) of PLLA decreased from 337 to 332 K and 450 to 445 K, respectively, suggesting that the compatibility of LEDPNR/ PLLA blend was enhanced by a reaction between the epoxy group of LEDPNR and the ester group of PLLA. The reaction was proved by high-resolution solid-state 13 C NMR spectroscopy.

The removal of proteins from natural rubber through a batch process was studied by the incubation of the rubber latex with urea in the presence of sodium dodecyl sulfate. Under suitable conditions, the total nitrogen content of deproteinized natural rubber (DPNR) decreased from 0.38 to 0.02 wt % after incubation for 10 min; this was similar to that of the rubber deproteinized with a proteolytic enzyme for 12 h. For applications, continuous incubation and centrifugation were individually investigated by the use of a semicircular channel and a continuous centrifuge, respectively, to scale up DPNR preparation.

The effect of the naturally occurring crosslinking junctions on green strength of natural rubber, isolated from Hevea brasiliensis, was investigated by using rubber extracted from Parthenium argentatum Gray (Guayule) as a model. Guayule rubber and natural rubber were characterized through nuclear magnetic resonance spectroscopy and size exclusion chromatography. The non‐rubber components of Guayule rubber and natural rubber were characterized by Kjeldahl method and Fourier transform infrared spectroscopy. It was found that Guayule rubber contains a much higher amount of fatty acids and their esters while it contains no proteins. The gel content, determined by swelling method, was related to a number of naturally occurring crosslinking junctions of Guayule rubber and natural rubber. The outstanding green strength of natural rubber was attributed to the effect of naturally occurring crosslinking junctions, when stress–strain curve and tensile properties of unvulcanized Guayule rubber were compared with those of unvulcanized natural rubber. Copyright © 2016 John Wiley & Sons, Ltd.

No abstract