Wound healing is a multifaceted process that possesses hemostasis, inflammation, proliferation, and remodeling stages. Diabetic wounds affect the transition of the organized phases and result in delayed healing due to...
Hyaluronic acid (HA) based hydrogels are one of most functional natural biomaterials in the field of cartilage tissue engineering (CTE). Even with the promising advantages of HA hydrogels, the complicated mechanical properties of the native cartilage have not been realized, and fabricating HA hydrogels with excellent mechanical properties to make them practical in CTE still remains a current challenge. Here, a strategy that integrates hydrogels and nanomaterials is shown to form a HA hydrogel with sufficient mechanical loading for cartilage tissue production and recombination. Cellulose nanofibrils (CNFs) are promising nanomaterial candidates as they possess high mechanical strength and excellent biocompatibility. In this study, we developed methacrylate-functionalized CNFs that are able to photo-crosslink with methacrylated HA to fabricate HA/CNF nanocomposite hydrogels. The present composite hydrogels with a compressive modulus of 0.46 ± 0.05 MPa showed adequate compressive strength (0.198 ± 0.009 MPa) and restorability, which can be expected to employ as a stress-bearing tissue such as articular cartilage. Besides, this nanocomposite hydrogel could provide a good microenvironment for bone marrow mesenchymal stem cell proliferation, as well as chondrogenic differentiation, and exhibit prominent repair effect in the full-thickness cartilage defect model of SD rats. These results suggest that the HA/CNF nanocomposite hydrogel creates a new possibility for fabricating a scaffold in CTE.
Tympanic membrane (TM) perforation leads to persistent otitis media, conductive deafness, and affects life quality. Ointment medication may not be sufficient to treat TM perforation due to the lack of an underlying tissue matrix and thus requiring a scaffold-based application. The engineering of scaffold biointerface close to the matrix via tissue-specific decellularized extracellular matrix (dECM) is crucial in instructing cell behaviour and regulating cell-material interaction in the bioengineering domain. Herein, polycaprolactone (PCL) and TM-dECM (from SD rats) were combined in a different ratio in nanofibrous form using an electrospinning process and crosslinked via tannic acid. The histological and biochemical assays demonstrated that chemical and enzymatic decellularization steps removed cellular/immunogenic contents while retaining collagen and glycosaminoglycan. The morphological, physicochemical, thermomechanical, contact angle, and surface chemical studies demonstrated that the tannin crosslinked PCL/dECM nanofibers fine-tune biophysical and biochemical properties. The multifaceted crosslinked nanofibers hold the tunable distribution of dECM moieties, assembled into a spool-shaped membrane, and could easily insert into perforated sites. The dECM decorated fibers provide a preferable biomimetic matrix for L929 fibroblast adhesion, proliferation, matrix adsorption, and f-actin saturation, which could be crucial for bioengineering. Overall, dECM patterning, surface hydrophilicity, interconnected microporosities, and multifaceted nanofibrous biosystem modulate cell-scaffold performance and could open opportunities to reconstruct TM perforation in a biomimetic fashion.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.