Pyrolysis of straw pellets and wood strips was performed in a fixed bed reactor. The chars, solid products of thermal degradation, were used as potential materials for activated carbon production. Chemical and physical activation processes were used to compare properties of the products. The chemical activation agent KOH was chosen and the physical activation was conducted with steam and carbon dioxide as oxidising gases. The effect of the activation process on the surface area, pore volume, structure and composition of the biochar was examined. The samples with the highest surface area (1349.6 and 1194.4 m2/g for straw and wood activated carbons, respectively) were obtained when the chemical activation with KOH solution was applied. The sample with the highest surface area was used as an adsorbent for model wastewater contamination removal.
In this work, liquefied biomass from the Baltic Sea was used for the preparation of rigid polyurethane (PUR) foams. The biomass contained 10 wt% of Enteromorpha macroalgae and 90 wt% of Zostera marina seagrass characterized by a high content of cellulose. The influence of time, temperature and the type of solvent on the efficiency of the liquefaction process and properties of biopolyols was determined. Obtained materials were analyzed in terms of chemical structure, rheological properties, thermal stability and basic physical and mechanical properties. It was found that optimal parameters for liquefaction of used biomass were: temperature of 150°C, reaction time of 6 h and a solvent mixture containing glycerol and poly(ethylene glycol) in ratio of 50:50 (biopolyol 50G50P_150). Under these conditions, 78 wt% of biomass was liquefied and resulting biopolyol was characterized by a hydroxyl number of 650 mg KOH/g. Depending on the used solvent mixture and the liquefaction temperature, biopolyols showed the character of Newtonian or non-Newtonian liquids. Rigid PUR foams were obtained by substitution of petrochemical polyol with 10, 20 and 30 wt% of biopolyol. It was found that the addition of biopolyol to foams' formulations did not cause significant changes in their chemical structure, while mechanical strength and thermal stability were enhanced. The presented study confirms that biomass from the Baltic Sea can be used for the synthesis of biopolyols and rigid polyurethane foams.
This article covers new application for char as a carrier of phase-change materials (PCM) that could be used as an additive to building materials. Being composed of bio-char and PCM, the granulate successfully competes with more expensive commercial materials of this type, such as Micronal® PCM. As a PCM carrier, char that was obtained from the pyrolysis of chestnut fruit (Aesculus hippocastanum) with different absorbances of the model phase-change material, Rubitherm RT22, was tested. DSC analysis elucidated several thermal properties (such as enthalpy, phase transition temperature, and temperature peak) of those mixtures and the results were compared with a commercial equivalent, Micronal DS 5040 X. Comparative research, approximating realistic conditions, were also performed by cooling and heating samples in a form of coatings that were made from chars with different content of RT22. These results indicated that the use of char as a PCM carrier was not only possible, but also beneficial from a thermodynamic point of view and it could serve as an alternative to commercial products. In this case, adsorption RT22 into char allowed for temperature stabilization comparable to Micronal DS 5040 X with ease of use as well as the economic advantages of being very low cost to produce due to microencapsulation. Other advantage of the proposed solution is related with the application of char obtained from waste biomass pyrolysis as a PCM carrier, and using this product in building construction to improve thermal comfort and increase energy efficiency.
Tires, conveyor belts, floor mats, and shoe soles form a main-stream of rubber waste. The amount of these used materials continuously increases due to development of the rubber market. Therefore, pro-ecological utilization (i.e., energy recycling instead of burning) and recovering valuable and recyclable materials becomes an urgent necessity. In this regard, this work was devoted to the chemical recycling of selected used rubber products, and it especially explores the possibility of limonene production. Different types of waste rubber were characterized and pyrolyzed at microgram and laboratory scales, and the results were compared. Additionally, the pyrolysis of tires, the most significant stream of rubber waste, was also conducted in a semi-technical scale reactor. The effectiveness of limonene formation in the liquid fractions obtained from different types of waste rubber was compared.
The results of pyrolysis of pine chips and refuse derived fuel fractions are presented. The experiments were carried out in a pilot pyrolysis reactor. The feedstock was analyzed by an elemental analyzer and the X-ray fluorescence spectrometer to determine the elemental composition. To find out optimum conditions for pyrolysis and mass loss as a function of temperature the thermogravimetric analysis was applied. Gases from the thermogravimetric analysis were directed to the infrared spectrometer using gas-flow cuvette to online analysis of gas composition. Chemical composition of the produced gas was measured using gas chromatography with a thermal conductivity detector and a flame ionization detector. The product analysis also took into account the mass balance of individual products.
In this paper, novel rigid polyurethane foams modified with Baltic Sea biomass were compared with traditional petro-based polyurethane foam as reference sample. A special attention was focused on complex studies of microstructure, which was visualized and measured in 3D with high-resolution microcomputed tomography (microCT) and, as commonly applied for this purpose, scanning electron microscopy (SEM). The impact of pore volume, area, shape and orientation on appearance density and thermal insulation properties of polyurethane foams was determined. The results presented in the paper confirm that microcomputed tomography is a useful tool for relatively quick estimation of polyurethane foams’ microstructure, what is crucial especially in the case of thermal insulation materials.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.