The present study explores the possibilities of using locally available inexpensive waste prawn shell derived chitin reinforced and bioabsorbable polylactic acid (PLA) laminated composites to develop new materials with excellent mechanical and thermal properties for implantable application such as in bone or dental implant. Chitin at different concentration (1–20% of PLA) reinforced PLA films (CTP) were fabricated by solvent casting process and laminated chitin-PLA composites (LCTP) were prepared by laminating PLA film (obtained by hot press method) with CTP also by hot press method at 160 °C. The effect of variation of chitin concentration on the resulting laminated composite's behavior was investigated. The detailed physico-mechanical, surface morphology and thermal were assessed with different characterization technique such as FT-IR, XRD, SEM and TGA. The FTIR spectra showed the characteristic peaks for chitin and PLA in the composites. SEM images showed an excellent dispersion of chitin in the films and composites. Thermogravimetric analysis (TGA) showed that the complete degradation of chitin, PLA film, 5% chitin reinforced PLA film (CTP2) and LCTP are 98%, 95%, 87% and 98% respectively at temperature of 500 °C. The tensile strength of the LCTP was found 25.09 MPa which is significantly higher than pure PLA film (18.55 MPa) and CTP2 film (8.83 MPa). After lamination of pure PLA and CTP2 film, the composite (LCTP) yielded 0.265–1.061% water absorption from 30 min to 24 h immerse in water that is much lower than PLA and CTP. The increased mechanical properties of the laminated films with the increase of chitin content indicated good dispersion of chitin into PLA and strong interfacial actions between the polymer and chitin. The improvement of mechanical properties and the results of antimicrobial and cytotoxicity of the composites also evaluated and revealed the composite would be a suitable candidate for implant application in biomedical sector.
In this study, bioresorbable phosphate-based glass (PBG) fibers were used to reinforce poly(lactic acid) (PLA). PLA/PBG random mat (RM) and unidirectional (UD) composites were prepared via laminate stacking and compression molding with fiber volume fractions between 14% and 18%, respectively. The percentage of water uptake and mass change for UD composites were higher than the RM composites and unreinforced PLA. The crystallinity of the unreinforced PLA and composites increased during the first few weeks and then a plateau was seen. XRD analysis detected a crystalline peak at 16.6° in the unreinforced PLA sample after 42 days of immersion in phosphate buffer solution (PBS) at 37°C. The initial flexural strength of RM and UD composites was ∼106 and ∼115 MPa, whilst the modulus was ∼6.7 and ∼9 GPa, respectively. After 95 days immersion in PBS at 37°C, the strength decreased to 48 and 52 MPa, respectively as a result of fiber-matrix interface degradation. There was no significant change in flexural modulus for the UD composites, whilst the RM composites saw a decrease of ∼45%. The molecular weight of PLA alone, RM, and UD composites decreased linearly with time during degradation due to chain scission of the matrix. Short fiber pull-out was seen from SEM micrographs for both RM and UD composites.
In recent years, there has been increasing interest in developing green biocomposite for industrial wastewater treatment. In this study, prawn-shell-derived chitosan (CHT) and kaolinite rich modified clay (MC) were used to fabricate biocomposite beads with different compositions. Prepared composite beads were characterized by FTIR, and XRD, and SEM. The possible application of the beads was evaluated primarily by measuring the adsorption efficiency in standard models of lead (II) and methylene blue (MB) dye solution, and the results show a promising removal efficiency. In addition, the composites were used to remove Cr (VI), Pb (II), and MB from real industrial effluents. From tannery effluent, 50.90% of chromium and 39.50% of lead ions were removed by composites rich in chitosan and 31.50% of MB was removed from textile effluent by a composite rich in clay. Moreover, the composite beads were found to be activated in both acidic and basic media depending on their composition, which gives a scope to their universal application in dye and heavy metal removal from wastewater from various industries.
Eight compatibilizing agents were studied to investigate their effect on the quality of the interface between a phosphate glass fiber and a poly(lactic acid) (PLA) matrix. After application of the agents via dip-coating, the fibers were Soxhlet extracted to remove any unreacted compatibilizer. To assess the interface quality, single fiber tensile tests of treated fibers and interfacial shear strengths (IFSS) of single fiber composites (SFC) were assessed. Of the agents tested, Glycerol-2phosphate disodium pentahydrate (GP) and low molecular weight PLA with a sodium salt terminal group (PLA-Na) showed the highest IFSS values, which were significantly higher than those of the control. Oligomeric PLA with a carbox-ylic acid end group and alendronate sodium trihydrate also showed an improvement over the control fibers. The hydrolytic degradation of these single fiber composites was studied over 7 days in water at 37 C and a significant decrease in IFSS was observed in all cases, with the treated samples dropping to the level of the control. TGA and XPS analysis of the sized fibers showed that GP and PLA-Na had been applied successfully to the fiber surface. V C 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: [3082][3083][3084][3085][3086][3087][3088][3089][3090][3091][3092][3093][3094] 2010
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.