Two series of biomedical segmented polyurethanes (SPU) based on poly(epsilon-caprolactone) diol (PCL diol), 1,6-hexamethylene diisocyanate (HDI) or L: -lysine methyl ester diisocyanate (LDI) and three novel chain extenders, were synthesized and characterized. Chain extenders containing urea groups or an aromatic amino-acid derivative were incorporated in the SPU formulation to strengthen the hard segment interactions through either bidentate hydrogen bonding or pi-stacking interactions, respectively. By varying the composition of the hard segment (diisocyanate and chain extender), its structure was varied to investigate the structure-property relationships. The different chemical composition and symmetry of hard segment modulated the phase separation of soft and hard domains, as demonstrated by the thermal behavior. Hard segment association was more enhanced by using a combination of symmetric diisocyanate and urea-diol chain extenders. The hard segment cohesion had an important effect on the observed mechanical behavior. Polyurethanes synthesized using HDI (Series H) were stronger than those obtained using LDI (Series L). The latter SPU exhibited no tendency to undergo cold-drawing and the lowest ultimate properties. Incorporation of the aromatic chain extender produced opposite effects, resulting in polyurethanes with the highest elongation and tearing energy (Series H) and the lowest strain at break (Series L). Since the synthesized biodegradable SPU possess a range of thermal and mechanical properties, these materials may hold potential for use in soft tissue engineering scaffold applications.
a b s t r a c tTo these days, the production of a small diameter vascular graft (o6 mm) with an appropriate and permanent response is still challenging. The mismatch in the grafts mechanical properties is one of the principal causes of failure, therefore their complete mechanical characterization is fundamental. In this work the mechanical response of electrospun bilayered small-diameter vascular grafts made of two different bioresorbable synthetic polymers, segmented poly(ester urethane) and poly(L-lactic acid), that mimic the biomechanical characteristics of elastin and collagen is investigated. A J-shaped response when subjected to internal pressure was observed as a cause of the nanofibrous layered structure, and the materials used. Compliance values were in the order of natural coronary arteries and very close to the bypass gold standard-saphenous vein. The suture retention strength and burst pressure values were also in the range of natural vessels. Therefore, the bilayered vascular grafts presented here are very promising for future application as smalldiameter vessel replacements.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.