Ductile cast iron samples were austenitized at 927 ЊC and subsequently austempered for 30 minutes, 1 hour, and 2 hours at 260 ЊC, 288 ЊC, 316 ЊC, 343 ЊC, 371 ЊC, and 399 ЊC. These were subjected to a plane strain fracture toughness test. Fracture toughness was found to initially increase with austempering temperature, reach a maximum, and then decrease with further rise in temperature. The results of the fracture toughness study and fractographic examination were correlated with microstructural features such as bainite morphology, the volume fraction of retained austenite, and its carbon content. It was found that fracture toughness was maximized when the microstructure consisted of lower bainite with about 30 vol pct retained austenite containing more than 1.8 wt pct carbon. A theoretical model was developed, which could explain the observed variation in fracture toughness with austempering temperature in terms of microstructural features such as the width of the ferrite blades and retained austenite content. A plot of against y (X ␥ C ␥ ) 1/2 resulted in a 2 K IC straight line, as predicted by the model.
An investigation was carried out to examine the influence of microstructure on the plane strain fracture toughness of austempered ductile iron. Austempered ductile iron (ADI) alloyed with nickel, copper, and molybdenum was austenitized and subsequently austempered over a range of temperatures to produce different microstructures. The microstructures were characterized through optical microscopy and X-ray diffraction. Plane strain fracture toughness of all these materials was determined and was correlated with the microstructure. The results of the present investigation indicate that the lower bainitic microstructure results in higher fracture toughness than upper bainitic microstructure. Both volume fraction of retained austenite and its carbon content influence the fracture toughness. The retained austenite content of 25 vol pct was found to provide the optimum fracture toughness. It was further concluded that the carbon content of the retained austenite should be as high as possible to improve fracture toughness.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.