Poly (methyl 2-methylpropenoate) (PMMA) is one of the most widely accepted biomaterials due to its acceptable advantageous but the limitations associated with these materials make them far from being ideal. So, the present study is to achieve desirable flexural strength by reinforcing PMMA with E-glass fiber.
Aim
Determination of flexural strength of PMMA by varying the weight percentage of glass fiber (2.5 wt%, 5 wt%, 10 wt%), and by varying the aspect ratio (3 mm/20 µm, 6 mm/20 µm, 12 mm/20 µm) of glass fiber.
Materials and methods
Specimens prepared using a standard rectangular mold of 62 mm length, 10 mm breadth and 2.5 mm thickness. A total of 60 samples prepared (6 samples in each group) polymer—monomer ratio 2.4:1 by weight used to prepare samples. Flexural strength is tested using universal testing machine Instron. The microstructural analysis using scanning electron microscopy performed in order to understand the fiber matrix bonding. Detailed statistical analysis done by one-way ANOVA.
Results
Highest flexural strength is observed for the PMMA reinforced with 6 mm/20 µm fiber 2.5 wt%.
How to cite this article
Mathew M, Shenoy K, Ravishankar KS. Flexural Strength of E-glass-reinforced PMMA. Int J Experiment Dent Sci 2014;3(1):24-28.
Hydrogen plasma treatment on polypropylene fiber has a significant role in enhancing the adhesion between PMMA polymer matrix and the polypropylene fibers and thereby the flexural strength.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.