The present paper presents results on the effect of selected heat treatments on the phase stability of an experimental superferritic stainless steel grade produced via the hot isostatic pressing (HIP) process. Both deformed and undeformed specimens were subjected to a variety of heat treatments within the 650-950uC temperature range for aging times of 5 min-1000 h. The temperature region of microstructural consistency for the superferritic stainless steel grade that guarantees optimum mechanical and corrosion properties was determined. Intermetallic phases were found to precipitate under all chosen temperatures, but the length of heat treatment before precipitation occurred varied with temperature and amount of deformation. The formation of minor amounts of austenite was detected in cold deformed specimens heat treated at 850 and 750uC while for the undeformed specimens, such a presence was verified only for specimens heat treated at 850uC. Formation of austenite is always preceded by the formation of an intermetallic phase. It was confirmed as anticipated, that deformation increases the rate of intermetallic phase precipitation. Superferritic steels are natural candidate materials for naval applications and fabrication techniques, such as welding, involve elevated temperatures on components previously deformed during a shaping exercise, therefore it is vital that an assessment of microstructural consistency of this novel powder metallurgy superferritic steel is performed.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.