The microscopic mechanism of the matching effect in a superconductor, which manifested itself as the production of peaks or cusps in the critical current at specific values of the applied magnetic field, was investigated with Lorentz microscopy to allow direct observation of the behavior of vortices in a niobium thin film having a regular array of artificial defects. Vortices were observed to form regular and consequently rigid lattices at the matching magnetic field, at its multiples, and at its fractions. The dynamic observation furthermore revealed that vortices were most difficult to move at the matching field, whereas excess vortices moved easily.
When a magnetic field penetrates a superconductor, it forms lattices of thin filaments called magnetic vortices. If a current is applied, these vortices move if not pinned down, destroying the superconductivity. The spatiotemporal behavior of the vortices was observed in a niobium film with a square lattice of defects made by ion irradiation. The vortices formed a domain of lattices. When the intensity of the applied magnetic field was decreased, the vortices were driven out of the film across its edges; when the intensity was increased, the vortices were driven into the film. The lattice exhibited brief and intermittent flow in "rivers" along domain boundaries. The rivers did not always flow along the same paths because new lattice domain configurations emerged whenever the flow stopped.
Many superconductors do not entirely expel magnetic flux-rather, magnetic flux can penetrate the superconducting state in the form of vortices. Moving vortices create resistance, so they must be 'pinned' to permit dissipationless current flow. This is a particularly important issue for the high-transition-temperature superconductors, in which the vortices move very easily. Irradiation of superconducting samples by heavy ions produces columnar defects, which are considered to be the optimal pinning traps when the orientation of the column coincides with that of the vortex line. Although columnar defect pinning has been investigated using macroscopic techniques, it has hitherto been impossible to resolve individual vortices intersecting with individual defects. Here we achieve the resolution required to image vortex lines and columnar defects in Bi2Sr2CaCu2O8+delta (Bi-2212) thin films, using a 1-MV field-emission electron microscope. For our thin films, we find that the vortex lines at higher temperatures are trapped and oriented along tilted columnar defects, irrespective of the orientation of the applied magnetic field. At lower temperatures, however, vortex penetration always takes place perpendicular to the film plane, suggesting that intrinsic 'background' pinning in the material now dominates.
Superconductors can be used as dissipation-free electrical conductors as long as vortices are pinned. Vortices in high-temperature superconductors, however, behave anomalously, reflecting the anisotropic layered structure, and can move readily, thus preventing their practical use. Specifically, in a magnetic field tilted toward the layer plane, a special vortex arrangement (chain-lattice state) is formed. Real-time observation of vortices using high-resolution Lorentz microscopy revealed that the images of chain vortices begin to disappear at a much lower temperature, Td, than the superconducting transition temperature, Tc. We attribute this image disappearance to the longitudinal oscillation of vortices along the chains.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations –citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.