Samarium-doped ceria (SDC) and gadolinium-doped ceria (GDC) thin films were formed by e-beam vapor deposition on SiO2 substrate, changing the deposition rate and substrate temperature during the deposition. X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy dispersive X-Ray spectrometry (EDS) were employed in order to investigate the structure ad morphology of the films. A single Raman peak describing the structure of undoped CeO2 was observed at a frequency of 466 cm−1. Doping of cerium oxide with rare-earth elements shifted the peak to lower frequencies (for Sm—462 cm−1). This shift occurs due to the increased number of oxygen vacancies in doped cerium oxide and it depends on the size and concentration factor of the dopant. It was found that wavenumbers and their intensity differed for the investigated samples, even though the peaks resembled each other in shape. The indicated bands for doped ceria originated as a result of the Raman regime (F2g) of fluorite dioxide associated with the space group (Fm3m). The observed peak‘s position shifting to a lower frequency range demonstrates the symmetric vibrations of oxygen ions around Ce4+ ions in octahedra CeO8. Raman shift to the lower frequencies for the doped samples has two reasons: an increase in oxygen vacancies caused by doping cerium oxide with rare-earth materials and the size factor, i.e., the change in frequency Δω associated with the change in the lattice constant Δa.
In this work, scandia-doped zirconia (ScSZ) and scandia–alumina co-doped zirconia (ScSZAl) thin films were prepared by electron beam vapor deposition. X-ray diffraction (XRD) results indicated a presence of ZrO2 cubic phase structure, yet Raman analysis revealed the existence of secondary tetragonal and rhombohedral phases. Thus, XRD measurements were supported by Raman spectroscopy in order to comprehensively analyze the structure of formed ScSZ and ScSZAl thin films. It was also found that Al dopant slows down the formation of the cubic phase. The impedance measurements affirmed the correlation of the amount of secondary phases with the conductivity results and nonlinear crystallite size dependence.
Scandia alumina stabilized zirconia (ScAlSZ) thin films were deposited using e-beam evaporation, and the effects of deposition parameters on the structure and chemical composition were investigated. The analysis of thin films was carried out using Energy-dispersive X-ray spectroscopy (EDS), X-ray photoelectron spectroscopy (XPS), X-Ray Diffraction Analysis (XRD) and Raman spectroscopy methods. It was found that the chemical composition of ScAlSZ thin films was different from the chemical composition of the initial powder. Moreover, the Al concentration in thin films depends on the deposition rate, resulting in a lower concentration using a higher deposition rate. XPS analysis revealed that ZrOx, oxygen vacancies, high concentrations of Al2O3 and metallic Al exist in thin films and influence their structural properties. The crystallinity is higher when the concentration of Al is lower (higher deposition rate) and at higher substrate temperatures. Further, the amount of cubic phase is higher and the amount of tetragonal phase lower when using a higher deposition rate.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.