In the study, Al foams were produced using 6063 Al alloy casting dross and Boric acid. Foam materials were sintered at 130 ºC for 1 hour and at 550 ºC for 3 hours. The microstructure was analyzed with optical and scanning electron microscopes (SEM). Compression strength was measured with a compression tester. The porosity increased from 34.8% to 37.8%, the compressive strength increased from 12.43 MPa to 20.25 MPa, and the hardness increased from 98 HV to 115 HV with increasing dross amount.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.