The coatings of LiTaO3 material on p-type Si (100) substrates were fabricated by using Chemical Solution Deposition (CSD) technique. In the fabrication process, the spin coater is used to flatten the LiTaO3 solution on the p-type Si (100) substrates surface, which was set at 4000 rpm for 30 seconds. Furthermore, the coating on those substrates was annealed in the furnace (Nabertherm type B410) for 15 hours at 750°C, 800°C, and 850°C temperature. The study of crystalline structure was obtained through the X-Ray Diffraction (Shimadzu XRD-7000) measuring with the interval of angular diffraction 2θ from 10° to 80° in the increment of 0.02°. Moreover, the study of optical properties was observed using the spectrometer (Ocean Optics USB4000-UV-VIS). Based on the results of the study, obtained a hexagonal angle diffraction peak for the crystal structure, when viewed from the refractive index, the optical properties are sensitive to visible and ultraviolet light. The results of the crystalline structure and optical properties that are sensitive to visible and ultraviolet light can be used to improve the performance of satellite systems in the term of the optical remote sensing.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.