Composite poly-L-lactide acid-based scaffolds with hydroxyapatite (HAp) content up to 75 wt.% were fabricated via solution blow spinning. The influence of HAp concentration on structure, wettability, mechanical properties and chemical and phase composition of the produced materials was examined. It was found that with an increase of HAp content the average fiber diameter was increased, the uniaxial strength and relative elongation were reduced, while the phase composition and surface wettability did not change. The performance of the scaffolds during implantation in the parietal bone of a rat skull for a period from 15 to 90 days was studied. The materials have shown high ability to integrate with both soft and hard tissues. It was found that scaffolds with 25 wt.% HAp content significantly enhance osteogenesis during scarification (damage) of the periosteum. Overall, the fabricated scaffolds proved to be highly efficient for replacing bone defects in long tubular bones.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.