International audienceEndowing conventional hydrophobic poly(vinylidene fluoride) (PVDF) films with hydrophilic properties was conducted using electron beam irradiation. Grafting of acrylic acid (AA) in/onto pre-irradiated PVDF films was investigated. Reaction parameters, monomer concentration and inhibitor concentration were examined. Radiation grafted films (PVDF-g-PAA) were synthesized with various grafting yields ranging from 12 to 130 wt % in presence of Mohr's salt (25 wt %). Below 80 wt % of monomer concentration, the degree of swelling was found to increase with the grafting yield. The PAA was arranged randomly in all PVDF matrix (grafting through). Above 80 wt % of monomer concentration, the PAA was grafted only onto the surface of PVDF films leading to a highly dense layer of PAA. Grafting through or surface grafting processes were achieved by varying the water fraction in the initial monomer solution. Water molecule acts not only as a carrier for the monomer but also as a plasticizer expanding the film in the three dimensions. Evidences of grafting through and surface grafting were produced using FTIR in ATR mode, SEM coupled to X-ray detection and XPS. An accurate quantification of AA units was possible up to the micromole via a Cu 2C –EDTA complex analyzed by UV–vis spectroscopy.

Poly(vinylidene difluoride) (PVDF) films were irradiated by means of heavy ions (in the electronic stopping‐power range) and electrons. Both types of ionizing radiation induce in the polymer film ionizations and excitations, but swift heavy ions induce a huge density of excitations and ionizations along the ion path. Dose‐range goes from 0.3 to 40 MGy. Irradiations were performed with Kr ions in the presence of helium, hydrogen, deuterium, and oxygen. Fourier transform infrared (FTIR) transmission measurements show differences in the nature of the created defects. Triple bonds are characteristic of the Kr ion irradiation. Double bonds, isolated and conjugated, exist for both kinds of radiation, but concentrations are higher with the Kr radiation. The presence of oxygen during irradiation produces oxidization defects. Typical bands of hydroxyls and carbonyls can be seen, respectively, in the 3800‐3000 cm−1 zone and ca. 1850–1730 cm−1. The formation of conjugated double bonds is enhanced when the Kr irradiation is performed under an O2 atmosphere. © 1994 John Wiley & Sons, Inc.

No abstract

No abstract

No abstract

Poly(vinylidene fluoride) (b-PVDF) nanoporous membranes are obtained by heavy ion irradiation and track etching leading to cylindrical pores. Pores diameter measured by scanning electron microscopy and small angle neutron scattering lies in the 20-50 nm range. Electron paramagnetic resonance study gives evidence that radicals still remains in PVDF membrane after track-etching. These radicals allows acrylic acid polymerization to be initiated onto membrane. Radiografted and functionalized membranes are characterized using infrared spectroscopy and weighing. Finally, radiografted poly(acrylic acid) (PAA) has been selectively labeled by fluorophores and imaged by confocal laser scanning microscopy. Images show the localisation of PAA specifically inside nanopores.

No abstract