The magnetic properties of the recycled hydrogenation disproportionation desorption recombination (HDDR) Nd-Fe-B powder, doped with a low weight fraction of DyF3 nanoparticles, were investigated. Spark plasma sintering (SPS) was used to consolidate the recycled Nd-Fe-B powder blends containing 1, 2, and 5 wt.% of DyF3 grounded powder. Different post-SPS sintering thermal treatment conditions (600, 750, and 900 °C), for a varying amount of time, were studied in view of optimizing the magnetic properties and developing characteristic core-shell microstructure in the HDDR powder. As received, recycled HDDR powder has coercivity (HCi) of 830 kA/m, and as optimally as SPS magnets reach 1160 kA/m, after the thermal treatment. With only 1–2 wt.% blended DyF3, the HCi peaked to 1407 kA/m with the thermal treatment at 750 °C for 1 h. The obtained HCi values of the blend magnet is ~69.5% higher than the starting recycled HDDR powder and 17.5% higher than the SPS processed magnet annealed at 750 °C for 1 h. Prolonging the thermal treatment time to 6 h and temperature conditions above 900 °C was detrimental to the magnetic properties. About ~2 wt.% DyF3 dopant was suitable to develop a uniform core-shell microstructure in the HDDR Nd-Fe-B powder. The Nd-rich phase in the HDDR powder has a slightly different and fluorine rich composition i.e., Nd-O-F2 than in the one reported in sintered magnets (Nd-O-F). The composition of reaction zone-phases after the thermal treatment and Dy diffusion was DyF4, which is more abundant in 5 wt.% doped samples. Further doping above 2 wt.% DyF3 is ineffective in augmenting the coercivity of the recycled HDDR powder, due to the decomposition of the shell structure and formation of non-ferromagnetic rare earth-based complex intermetallic compounds. The DyF3 doping is a very effective single step route in a controlled coercivity improvement of the recycled HDDR Nd-Fe-B powder from the end of life magnetic products.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.