We present in this study a creep behavior in flexure of a hybrid composite consisting of a polyester matrix containing methyl methacrylate reinforced by two bidirectional fabrics. The first one is made with E-glass fibers and the second one is made of a knitted polyamide 66. The mass fractions are 13% for the glass fabric and 9% for the polyamide fabric. The specimens, of dimensions (L = 60, l = 15 and h = 2.3 mm) containing 06 alternating layers (2P/2V/2P) were fabricated by using the vacuum bag molding method. Bending tests performed at different temperatures allowed us first to determine the load levels for the creep tests. Creep tests at different loads (5 to 43 MPa) and different temperatures (23 ° to 80 ° C) show a noticeable increase of creep deformation for both tests under the same load and different temperatures just as those carried out at different loads under the same temperature. The initial deformation varies significantly with the load but very little with temperature. The application of the Findley model shows good correlation with experimental results. Model parameters were identified. Creep deformation satisfies the principle of superposition time-temperature-stress (TTSSP). Findley's model has subsequently been coupled with the principle of superposition of time-temperature-stress to plot master curves at different stresses and temperatures; this enables prediction of creep deformation in the long term.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.