SUMMARYβ-FeSi 2 thin films were grown on Si(111) substrates by pulsed laser deposition (PLD) method using a Nd:YAG laser (λ = 1064 nm, laser energy = 50 mJ, laser energy density = 1.65 J/cm 2 , repetition frequency = 10 Hz). In the fabrication process, three targets of (a) Fe(5N), (b) FeSi 2 (3N), and (c) Fe(5N) + FeSi 2 (3N) were used. The β-FeSi 2 thin films having the best properties of crystallinity were obtained in the case of (c), in which the first layer as the template was formed with the target of Fe(5N) and then, on top of that, the second layer was deposited with the target of FeSi 2 (3N). At this time, it was found that by XRD measurement, the degree of crystallinity of the films of case (c) in which the first layer was introduced as the template improved 1.4 times as much compared with case (a), and that by SEM and AFM observations, surface morphologies also improved. Moreover, it was found that by TEM observation, the β-FeSi 2 thin films grew uniformly along the direction of (220) or (202) from the interface of the Si substrate and the film to the free surface and that by EDS analysis, the compositions of Fe and Si were uniformly distributed.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.