Highly lattice-mismatch (over 8%) ternary InxGa1-xSb alloy directly grown on GaAs substrates was demonstrated by metalorganic chemical vapor deposition (MOCVD). The influence of growth parameters, such as growth temperature, indium vapor composition, and V/III ratio, on the film properties was investigated, and it was found that the growth temperature has the strongest effect on the surface morphology and the crystal quality of the InxGa1-xSb epilayer. An optimized growth temperature of ∼590 °C and a V/III ratio of 2.5 were used for the growth of the InxGa1-xSb epilayer on GaAs that displays a lower surface roughness. High-resolution transmission electron microscopy micrographs exhibit that InxGa1-xSb epilayer growth on GaAs was governed by the interfacial misfit dislocation growth mode. Furthermore, the variation of the intermixing layer thickness at the InxGa1-xSb/GaAs heterointerface was observed. These results provide an information of growing highly lattice-mismatched epitaxial material systems by MOCVD growth process.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.