In the current study, the thermodynamics of the slag-metal equilibrium reaction between Inconel 718 Ni-based alloy and CaF2-CaO-Al2O3-MgO-TiO2 electroslag remelting (ESR)-type slags were systematically investigated in the temperature range from 1773 to 1973 K (1500 to 1700 °C). The equilibrium Al content increased with increasing temperature, whereas the equilibrium Ti content decreased with increasing temperature at a fixed slag composition. The important factors for controlling the oxidation of Al and Ti in the Inconel 718 superalloy were TiO2 > Al2O3 > CaO > CaF2 > MgO in ESR-type slag and Al > Ti in a consumable electrode. The conventional method of sampling by means of a quartz tube could result in contamination of the molten metal and changes in the size of the “special reaction interface”. Therefore, a novel method was used in the present study to investigate the slag-metal reaction kinetics to accurately obtain the kinetic parameters. The mass transfer coefficient was determined by coupling with the kinetic model derived from the assumption that the reaction rate ([Al] + (TiO2) = [Ti] + (Al2O3)) was controlled by the mass transfer of [Ti], [Al], (TiO2) and (Al2O3) in the boundary layer, respectively.
Abstract:The influences of austenitizing conditions on the microstructure of AISI M42 high-speed steel were investigated through thermodynamic calculation, microstructural analysis, and in-situ observation by a confocal scanning laser microscope (CSLM). Results show that the network morphology of carbides could not dissolve completely and distribute equably in the case of the austenitizing temperature is 1373 K. When the austenitizing temperature reaches 1473 K, the excessive increase in temperature leads to increase in carbide dissolution, higher dissolved alloying element contents, and unwanted grain growth. Thus, 1453 K is confirmed as the best austenitizing condition on temperature for the steel. In addition, variations on the microstructure and hardness of the steel are not obvious when holding time ranges from 15 to 30 min with the austenitizing temperature of 1453 K. However, when the holding time reaches 45 min, the average size of carbides tends to increase because of Ostwald ripening. Furthermore, the value of M s and M f decrease with the increase of cooling rate. Hence, high cooling rate can depress the martensitic transformation and increase the content of retained austenite. As a result, the hardness of the steel is the best (65.6 HRc) when the austenitizing temperature reaches 1453 K and is held for 30 min.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.