Tissue engineering has become a new approach for repairing bone defects. Previous studies indicated that coral scaffolds had been utilized with bone marrow stromal cells (BMSCs) in a variety of approaches for bony reconstruction. In these applications, the degradation rate of the material did not match the rate at which bone was regenerated. In this study, a previously established 30 mm long mandibular segmental defect was repaired with engineered bone using green fluorescent protein-labeled osteogenic BMSCs seeded on porous coral (n = 12). Defects treated with coral alone (n = 12) were used as an experimental control. In the BMSCs/coral group, new bone formation was observed from 4 weeks postoperation, and bony-union was achieved after 32 postoperative weeks. The residual coral volume of the BMSCs/coral grafts at 12 weeks (20-30%) was significantly higher than that at 32 weeks (10-15%, p < 0.05), which was detected by microcomputed tomography and histological examination. The engineered bone with BMSCs/coral achieved satisfactory biomechanical properties at 32 weeks postoperation, which was very close to that of the contralateral edentulous mandible. More importantly, immunostaining demonstrated that the implanted BMSCs differentiated into osteoblast-like cells. In contrast, minimal bone formation with almost solely fibrous connection was observed in the group treated with coral alone. Based on these results, we conclude that engineered bone from osteogenically induced BMSCs and biodegradable coral can successfully repair the critical-sized segmental mandibular defects in canines and the seeding cells could be used for bony restoration.
Inflammation is part of the natural healing response, but persistent inflammatory events tend to contribute to pathology changes of tendon or ligament. Phenotypic switching of macrophages within the inflammatory niche is crucial for tendon healing. One viable strategy to improve the functional and biomechanical properties of ruptured tendons is to modulate the transition from inflammatory to regenerative signals during tendon regeneration at the site of injury. Here, we developed a tendon repair scaffold made of biodegradable polycaprolactone by electrospinning, which was modified to deliver Wnt3a protein and served as an implant to improve tendon healing in a rat model of Achilles tendon defect. During the in vitro study, Wnt3a protein promoted the polarization of M2 macrophages. In the in vivo experiment, Wnt3a scaffold promoted the early recruitment and counting curve of macrophages and increased the proportion of M2 macrophages. Achilles function index and mechanical properties showed that the implantation effect of the Wnt3a group was better than that of the control group. We believe that this type of scaffold can be used to repair tendon defects. This work highlights the beneficial role of local delivery of biological factors in directing inflammatory responses toward regenerative strategies in tendon healing.
Implant-supported cement-screw-retained crowns combine the advantages of screw-retained and cement-retained crowns. However, the occlusal screw access hole interrupts porcelain integrity, which may result in porcelain cracks or fractures. There is insufficient scientific evidence to prove that screw access holes affect the fracture load of implant-supported monolithic zirconia crowns. In this study, we investigated the effects of the screw access hole and its preparation technique on the fracture load of implant-supported monolithic zirconia single crown. The crowns were designed for the maxillary right first premolar. Three techniques analysed for screw access hole preparations included computer-aided designed/ computer-aided manufactured (CAD/CAM) before sintering, manually prepared after sintering, and then resintering. Our findings show that the screw access holes and preparation techniques have no significant effects on the fracture load of implant-supported monolithic zirconia single crown. On the other hand, the screw access hole preparation techniques affect failure initiation in implant-supported monolithic zirconia single crown.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.