Increasingly more young patients have been submitted to reconstruction of the Temporomandibular Joint (TMJ), so, the prostheses must to present more functional longevity. Objective: To evaluate the effect of diamond-like carbon film (DLC) over titanium alloy (Ti6Al4V) and polyethylene (UHWPE) samples, their mechanical and chemical properties and cellular cytotoxicity. Methods: Titanium and UHWPE specimens, with 2.5 cm in diameter and 2 mm thickness were coated through plasma enhanced chemical vapor deposition (PECVD) with DLC or DLC doped with silver (DLC-Ag). Scanning electron microscopy (SEM) morphological analysis, Energy-dispersive spectroscopy (EDS) chemical analysis, scratching test, mechanical fatigue test, surface roughness analysis, and cellular cytotoxicity were performed. Data were statistically analyzed using one-way ANOVA (p < 0.05) or two-way ANOVA and multiple comparison Tukey test. Results: In the SEM analysis, morphological differences were observed on substrates after DLC deposition. The film chemically modified the substrate surfaces, according to the EDS analysis. The initial critical load failure occurred at 6.1 N for DLC and 9.7 N for the DLC-Ag film. The DLC film deposition over the polyethylene promoted a decrease in the polymer's damaged area after mechanical fatigue cycling. The cytotoxicity analysis demonstrated less biocompatibility in experimental groups, when compared to control, however, increased biocompatibility was observed, at 10 days, in all groups. Conclusion: The diamond-like carbon coating enhanced the chemical and mechanical properties from substrates, however modified biological interaction course of the titanium alloy (Ti6Al4V) and polyethylene (UHWPE) samples. Parameters for film deposition remain to be improved in order to obtain best biocompatibility.
Diamond-like carbon (DLC) film is a biocompatible hard coating material that can prevent the leaching of metal ions. This study evaluates the structural characteristics of DLC, with and without silver nanoparticles, deposited by plasma (PECVD) on titanium alloy (Ti-6Al-4V) and bone formation in contact with DLC films. Sixty Ti-6Al-4V samples were used divided in: uncoated, coated with DLC and coated with DLC-Ag. After structural characterization, samples were fixed bilaterally at the rabbit's mandible. After 15 and 90 days, samples were characterized again and bone formation in the area was analyzed by histomorphometry. Statistical analysis was performed by two-way ANOVA. Both the DLC and DLC-Ag films were firmly adhered and showed a high electrical resistance without significant changes in the Raman spectrum after in vivo integration. After 15 days, there were immature bone trabeculae in the interface and partially covering the surface. After 90 days, mature bone filled the interface and coved the surface. There was no statistically significant difference among the three groups in both periods. In conclusion, osseointegration with DLC, DLC-Ag and uncoated Ti-6Al-4V is similar. However, DLC and DLC-Ag coverings have the advantage of electrical insulation and can presumably control bacterial activity and ion leaching.
Lymphatic dissemination is one of the most important pathways for metastasis in many solid tumors, including head and neck carcinomas. The lymphatic growth of cancer has been used as a significant independent adverse prognostic factor and provides information about tumor progression. Salivary gland tumors present different prognoses and have the ability to develop metastases; however, this information regarding the lymphatic spread is scarce. This paper quantifies the lymphatic microvessel density (LMD) in benign and malignant salivary gland tumors and analyzes the relationship between LMD and tumor expression of vascular endothelial growth factors C (VEGF-C) and the proliferative index. The results show that there is no correlation between LMD, VEGF-C and the proliferative index in the majority of salivary gland tumors analyzed, apart from polymorphous low-grade carcinoma which exhibits statistical correlation between LMD and the proliferative index (p < 0.05). This correlation probably does not indicate a poor prognosis for this PLGA, since this is a low metastasizing carcinoma of the salivary glands. Different from other solid tumors, such as breast or prostatic carcinomas, there is no correlation between VEGF-C and LMD in salivary gland tumors, and so these traits are not able to estimate the metastatic risk or the prognosis of these tumors.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.