We have investigated a novel method of remotely switching the conformation of a weak polybase brush using an applied voltage. Surface-grafted polyelectrolyte brushes exhibit rich responsive behavior and show great promise as "smart surfaces", but existing switching methods involve physically or chemically changing the solution in contact with the brush. In this study, high grafting density poly(2-(dimethylamino)ethyl methacrylate) (PDMAEMA) brushes were grown from silicon surfaces using atom transfer radical polymerization. Optical ellipsometry and neutron reflectivity were used to measure changes in the profiles of the brushes in response to DC voltages applied between the brush substrate and a parallel electrode some distance away in the surrounding liquid (water or D(2)O). Positive voltages were shown to cause swelling, while negative voltages in some cases caused deswelling. Neutron reflectometry experiments were carried out on the INTER reflectometer (ISIS, Rutherford Appleton Laboratory, UK) allowing time-resolved measurements of polymer brush structure. The PDMAEMA brushes were shown to have a polymer volume fraction profile described by a Gaussian-terminated parabola both in the equilibrium and in the partially swollen states. At very high positive voltages (in this study, positive bias means positive voltage to the brush-bearing substrate), the brush chains were shown to be stretched to an extent comparable to their contour length, before being physically removed from the interface. Voltage-induced swelling was shown to exhibit a wider range of brush swelling states in comparison to pH switching, with the additional advantages that the stimulus is remotely controlled and may be fully automated.
Film embrittlement criteria were determined for photo-oxidative degradation of linear low density polyethylene (LLDPE) films by using a range of characterisation techniques: tensile, high-temperature GPC, MAS-NMR, FTIR-ATR, WAXS and SAXS. The key embrittlement criteria was the loss of 95% elongation at break and the reduction in interlamellar distance, reduced down to approximately 30e50 A, as a result of recrystallisation of mobile short chain fragments produced from chain scission reaction. Interlamellar thinning correlated well with the changes in double yield points seen in the tensile data, where the absence of the second yield point signified that the tie molecules at the lamellar interface underwent chain scission and could no longer transfer the tensile stress to reach c-axis slip of the lamellar crystals. This was also supported by a reduction in amorphouselamellar interfacial width with ageing time, extracted from SAXS data using the linear correlation function.
Nanocrystal quantum dots are generally coated with an organic ligand layer. These layers are a necessary consequence of their chemical synthesis, and in addition they play a key role in controlling the optical and electronic properties of the system. Here we describe a method for quantitative measurement of the ligand layer in 3 nm diameter lead sulfide–oleic acid quantum dots. Complementary small-angle X-ray and neutron scattering (SAXS and SANS) studies give a complete and quantitative picture of the nanoparticle structure. We find greater-than-monolayer coverage of oleic acid and a significant proportion of ligand remaining in solution, and we demonstrate reversible thermal cycling of the oleic acid coverage. We outline the effectiveness of simple purification procedures with applications in preparing dots for efficient ligand exchange. Our method is transferrable to a wide range of colloidal nanocrystals and ligand chemistries, providing the quantitative means to enable the rational design of ligand-exchange procedures.
The layer-by-layer (L-b-L) deposition of oppositely charged polyelectrolytic macroinitiators has been demonstrated on planar silica substrates. The build-up of the macroinitiator multilayers was monitored by ellipsometry (up to 21 layers) and dual polarization interferometry (up to 17 layers) and good agreement was found between these techniques. The increase in L-b-L thickness was approximately linear, with an average thickness of 2.3 A per layer of deposited macroinitiator. Surface-initiated ATRP of a model nonionic methacrylic monomer, 2-hydroxyethyl methacrylate (HEMA) in a 1:1 methanol/water mixture was conducted at ambient temperature. Increasing the number of macroinitiator layers led to a significant increase in PHEMA brush thickness up to 110 nm, which is attributed to the greater surface grafting density. PHEMA brush thicknesses obtained after 22 h showed a linear dependence on the number of layers of deposited macro-initiator, with all layers exhibiting near-identical growth kinetics. X-ray photoelectron spectroscopy was used to monitor L-b-L assembly and also to confirm PHEMA growth. This technique indicated the loss of small counterions from the multilayers during L-b-L deposition and confirmed an increase in the surface density of bromoester initiator groups as the number of deposited macroinitiator layers was increased. For 17 macroinitiator layers, the bromoester initiator density is estimated to be approximately 4.9 +/- 0.2 nm (-2) from the DPI data. This is comparable to that calculated for ATRP initiator monolayers obtained by either thiol or silane chemistry. Ellipsometry suggested that the macroinitiator multilayers were weakly hydrated prior to the in situ HEMA polymerization. AFM studies indicated that the PHEMA brushes had appreciable surface roughness, but this roughness became negligible compared to the brush thickness with increasing macroinitiator layers.
All-atom molecular dynamics simulations and experimental characterization have been used to examine the structure and dynamics of novel evaporation-suppressing films where the addition of a water-soluble polymer to an ethylene glycol monooctadecyl ether monolayer leads to improved water evaporation resistance. Simulations and Langmuir trough experiments demonstrate the surface activity of poly(vinyl pyrrolidone) (PVP). Subsequent MD simulations performed on the thin films supported by the PVP sublayer show that, at low surface pressures, the polymer tends to concentrate at the film/water interface. The simulated atomic concentration profiles, hydrogen bonding patterns, and mobility analyses of the water-polymer-monolayer interfaces reveal that the presence of PVP increases the atomic density near the monolayer film, improves the film stability, and reduces the mobility of interfacial waters. These observations explain the molecular basis of the improved efficacy of these monolayer/polymer systems for evaporation protection of water and can be used to guide future development of organic thin films for other applications.
We study the conformations of polymer chains in polymer−graphene oxide nanocomposites. We show that the chains have a reduced radius of gyration that is consistent with confinement at a solid interface in the melt, as is expected for well-dispersed, high aspect ratio nanoparticles that are much larger than the polymer coil size. We show that confinement of the polymer chains causes a corresponding reduction in interchain entanglements, and we calculate a contribution to the plateau modulus from the distorted polymer network via a simple scaling argument. Our results are a significant step forward in understanding how two-dimensional nanoparticles affect global material properties at low loadings.
Abstract:Responsive polymer brushes possess many interesting properties that enable them to control a range of important interfacial behaviours, including adhesion, wettability, surface adsorption, friction, flow and motility. The ability to design a macromolecular response to a wide variety of external stimuli makes polymer brushes an exciting class of functional materials, and has been made possible by advances in modern controlled polymerization techniques. In this review we discuss the physics of polymer brush response along with a summary of the techniques used in their synthesis. We then review the various stimuli that can be used to switch brush conformation; temperature, solvent quality, pH and ionic strength as well as the relatively new area of electric field actuation We discuss examples of devices that utilise brush conformational change, before highlighting other potential applications of responsive brushes in real world devices.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.