PURPOSEPolymer infiltrated ceramic network (PICN) materials, also called hybrid ceramics, are new materials in dental market. The manufacturer of the PICN material VITA Enamic suggests 3 different finishing procedures for this new material. In the present study, surface roughness and color differences caused from different finishing procedures of VITA Enamic were investigated.MATERIALS AND METHODS120 specimens were prepared in dimensions 2 × 10 × 12 mm from VITA Enamic hybrid ceramic blocks with 'high translucency' and 'translucency 2M2' shades. The specimens were divided into 8 groups. For each group, different finishing procedures suggested by the manufacturer were performed. Surface roughness values were determined by a tactile portable profilometer. Color changes were evaluated using a clinical spectrophotometer. The data were analyzed using one-way ANOVA and Tukey's post-hoc comparison. The significance level was set at α=0.05.RESULTSThe roughest surfaces were observed in Glaze Groups. Their surface roughness values were similar to that of the control group. Clinical Kit and Technical Kit groups did not show a statistically significant difference regarding surface roughness (P>.05). The largest color difference regarding ΔE00 was observed in Clinical Kit finishing groups. There were also statistically significant color changes between the groups (P<.05). However, all the groups showed clinically acceptable color change (ΔE00<2.25) except Clinical Kit Groups (ΔE00>2.25).CONCLUSIONWithin the limitations of the present study, it may be suggested that finishing the VITA Enamic restorations by Technical Kit instead of Glaze and Clinical Kit gives better clinical performance in regard to surface roughness and shade matching.
PURPOSEBeverages may affect the translucency of esthetic dental restorative materials. The aim of the present study was to investigate the effects of coffee and red wine on the translucency of a PICN material with two translucency levels, and finished with different methods.MATERIALS AND METHODS2M2 high translucent and translucent VITA Enamic hybrid ceramic blocks were investigated. Rectangular specimens with the dimensions of 12 mm × 14 mm × 2 mm were prepared. The specimens were finished and polished with different methods as suggested by the manufacturer. The translucency parameters of the specimens were evaluated before and after 24 hours, 7 days, and 28 days immersion in distilled water, coffee and red wine. Translucency parameters were measured using a portable spectrophotometer.RESULTSAt the end of 28 days, there was no statistically significant difference between the groups of specimens kept in coffee (P>.05). In the red wine groups, there was a statistically significant difference between the control group and all other groups (P<.05) at the end of 28 days.CONCLUSIONThe translucency of hybrid ceramic for a restoration may not be important regarding the effects of coffee on translucency change because the specimens with different translucencies and finishing methods that were immersed to coffee had similar translucency parameters at the end of 28 days. The translucency of hybrid ceramic may be important in the case of red wine, however, since the results showed that highly translucent specimens exposed to red wine demonstrated better translucency parameters than specimens made from translucent blocks at the end of 28 days.
This study intended to analyze microcracks and fractographic markings on the surface of all ceramic crowns after milling and compare the fracture loads. 90 crowns were manufactured from two feldspathic (Priticrown-Pr and Vita Mark II-Vi) and a lithium disilicate (EmaxCAD-Em) blocks (n = 30). Two groups (n = 15) were prepared for each ceramic. In the first group, crowns were analyzed twice via the fluorescent penetrant method for microcrack detection, after the manufacturing process and thermal cycles. The load to fracture test was applied at a crosshead speed of 0.5 mm/min until catastrophic failure. Second group crowns were directly cemented onto the Co-Cr dies following the manufacturing process and loaded to fracture. Fractographic markings were analyzed through scanning electron microscope. Spearman correlation analysis, Kruskal-Wallis H test, Mann-Whitney U test, and Wilcoxon Signed Rank test were applied (α = .05). Fracture loads of Em crowns were higher than other groups (p < .05), with and without the aging procedure. Except for second group Pr (r = −.532), no significant relationship was found between microcrack numbers and fracture loads (p > .05). Thermal cycling did not affect microcrack numbers and fracture loads (p > .05). Tooth-shaped multilayered Pr blocks did not provide an advantage in terms of microcrack and fracture loads.
This study intended to compare the repair bond strength of computer-aided design/ computer-aided manufacturing (CAD/CAM) blocks consisting of resin and feldspathic ceramics following different surface treatments using the microtensile bond strength (μTBS) test. Ten specimens were prepared with 4 mm height for Vita Enamic (VE), Lava Ultimate (LU), Vita Mark II (VM), and thermocycled (10,000 cycle, 5-55 C). Each material was categorized into one of five subgroups according to following surface treatments: (a) bur grinding (BG), (b) hydrofluoric acid etching (HF), (c) neodymiumdoped yttrium aluminum garnet (Nd:YAG or NY), (d) erbium-doped yttrium aluminum garnet (Er:YAG or EY), and (e) erbium, chromium-doped yttrium, scandium, gallium, and garnet (Er,Cr:YSGG or ECY) laser conditioning. After surface treatment procedures, specimens were properly restored to 4 mm high with a micro-hybrid composite resin. Bar specimens (1 × 1 × 8 mm) were obtained using a low-speed cutting machine and then thermocycled (10,000 cycle, 5-55 C). The μTBS was tested at 1 mm/min crosshead speed, and failure modes were evaluated. Data were analyzed with two-way ANOVA and post hoc Tukey tests. LU-BG showed significantly higher μTBS (32.94 ± 5.80 MPa) compared to LU-laser groups (p < .05). VE-BG showed significantly higher μTBS (22.06 ± 4.26 MPa) compared to other VE groups (p < .05). Among the laser groups, the NY laser produced the lowest (p < .05) μTBS for LU (13.42 ± 3.44 MPa) and VE (2.27 ± 0.85 MPa), while EY showed the highest (p < .05).Laser-treated VM groups were all prefailured. VM-HF produced a higher μTBS (18.73 ± 3.75 MPa) than VM-BG (5.05 ± 1.76 MPa) (p < .05).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.