There is a large difference in strength between ovine and bovine leather. The structure and arrangement of fibrous collagen in leather and the relationship between collagen structure and leather strength has until now been poorly understood. Synchrotron based SAXS is used to characterize the fibrous collagen structure in a series of ovine and bovine leathers and to relate it to tear strength. SAXS gives quantitative information on the amount of fibrous collagen, the orientation (direction and spread) of the collagen microfibrils, and the d-spacing of the collagen. The amount of collagen varies through the thickness of the leather from the grain to the corium, with a greater concentration of crystalline collagen measured toward the corium side. The orientation index (OI) is correlated strongly with strength in ovine leather and between ovine and bovine leathers. Stronger leather has the fibrils arranged mostly parallel to the plane of the leather surface (high OI), while weaker leather has more out-of-plane fibrils (low OI). With the measurement taken parallel to the animal's backbone, weak (19.9 N/mm) ovine leather has an OI of 0.422 (0.033), stronger (39.5 N/mm) ovine leather has an OI of 0.452 (0.033), and bovine leather with a strength of (61.5 N/mm) has an OI of 0.493 (0.016). The d-spacing profile through leather thickness also varies according to leather strength, with little variation being detected in weak ovine leather (average=64.3 (0.5) nm), but with strong ovine leather and bovine leather (which is even stronger) exhibiting a dip in d-spacing (from 64.5 nm at the edges dropping to 62 nm in the center). This work provides a clear understanding of a nanostructural characteristic of ovine and bovine leather that leads to differences in strength.
Collagen is the main structural component of leather, skin, and some other applications such as medical scaffolds. All of these materials have a mechanical function, so the manner in which collagen provides them with their strength is of fundamental importance and was investigated here. This study shows that the tear strength of leather across seven species of mammals depends on the degree to which collagen fibrils are aligned in the plane of the tissue. Tear-resistant material has the fibrils contained within parallel planes with little crossover between the top and bottom surfaces. The fibril orientation is observed using small-angle X-ray scattering in leather, produced from skin, with tear strengths (normalized for thickness) of 20-110 N/mm. The orientation index, 0.420-0.633, is linearly related to tear strength such that greater alignment within the plane of the tissue results in stronger material. The statistical confidence and diversity of animals suggest that this is a fundamental determinant of strength in tissue. This insight is valuable in understanding the performance of leather and skin in biological and industrial applications.
The distribution and effect of applied strain on the collagen fibrils that make up leather may have an important bearing on the ultimate strength and other physical properties of the material. While sections of ovine and bovine leather were being subjected to tensile strain up to rupture, synchrotron-based small-angle X-ray scattering (SAXS) spectra were recorded edge-on to the leather at points from the corium to the grain. Measurements of both fibril orientation and collagen d spacing showed that, initially, the fibers reorient under strain, becoming more aligned. As the strain increases (5-10% strain), further fibril reorientation diminishes until, at 37% strain, the d spacing increases by up to 0.56%, indicating that significant tensile forces are being transmitted to individual fibrils. These changes, however, are not uniform through the cross-section of leather and differ between leathers of different strengths. The stresses are taken up more evenly through the leather cross-section in stronger leathers in comparison to weaker leathers, where stresses tended to be concentrated during strain. These observations contribute to our understanding of the internal strains and structural changes that take place in leather under stress.
Ovine forestomach matrix (OFM) is a native and functional decellularized extracellular matrix biomaterial that supports cell adhesion and proliferation and is remodeled during the course of tissue regeneration. Small angle X-ray scattering demonstrated that OFM retains a native collagen architecture (d spacing = 63.5 ± 0.2 nm, orientation index = 20°). The biophysical properties of OFM were further defined using ball-burst, uniaxial and suture retention testing, as well as a quantification of aqueous permeability. OFM biomaterial was relatively strong (yield stress = 10.15 ± 1.81 MPa) and elastic (modulus = 0.044 ± 0.009 GPa). Lamination was used to generate new OFM-based biomaterials with a range of biophysical properties. The resultant multi-ply OFM biomaterials had suitable biophysical characteristics for clinical applications where the grafted biomaterial is under load.
As hides and skins are processed to produce leather, chemical and physical changes take place that affect the strength and other physical properties of the material. The structural basis of these changes at the level of the collagen fibrils is not fully understood and forms the basis of this investigation. Synchrotron-based small-angle X-ray scattering (SAXS) is used to quantify fibril orientation and D-spacing through eight stages of processing from fresh green ovine skins to staked dry crust leather. Both the D-spacing and fibril orientation change with processing. The changes in thickness of the leather during processing affect the fibril orientation index (OI) and account for much of the OI differences between process stages. After thickness is accounted for, the main difference in OI is due to the hydration state of the material, with dry materials being less oriented than wet. Similarly significant differences in D-spacing are found at different process stages. These are due also to the moisture content, with dry samples having a smaller D-spacing. This understanding is useful for relating structural changes that occur during different stages of processing to the development of the final physical characteristics of leather.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.