Inconel 625 is a nickel-based alloy that is mainly used in high-temperature applications. Inconel 625 exhibits an unstable plastic flow at elevated temperatures characterized by serrated yielding, well-known as the Portevin-Le Chatelier effect. The evaluation of the mechanical properties of Inconel 625 at high temperatures is the aim of this work. The tensile tests were executed in temperatures ranging from room temperature to 1000 °C with strain rates of 2 × 10−4 to 2 × 10−3 s−1. The creep tests were executed in the temperature range of 600–700 °C and in the stress range of 500–600 MPa in a constant load mode. The optical and scanning electron microscopes were used for surface fracture observation. In the curves obtained at 200–700 °C the serrated stress-strain behavior was observed, which was related to the dynamic strain aging effect. The yield strength and the elongation values show anomalous behavior as a function of the test temperature. An intergranular cracking was observed for a specimen tensile tested at 500 °C that can be attributed to the decohesion of the carbides along the grain boundaries. The fracture surface of the specimen tensile tested at 700 °C showed the predominance of transgranular cracking with tear dimples with a parabolic shape.
The Inconel 625 is a nickel-based alloy has been widely used in the high-temperature application. The Inconel 625 exhibits unstable plastic flow at elevated temperature characterized by serrated yielding, known as Portevin-Le Chatelier effect. The aim of this work is to evaluate the mechanical properties at high temperatures of the Inconel 625. The tensile tests were performed in the temperature range of room temperature until 1000 °C and strain rate of 2x10^-4 to 2x10^-3 s^-1. The creep tests were performed in the temperature range of 600-700 °C, in the stress range of 500-600 MPa in a constant load mode. The surface fracture was observed by optical and scanning electron microscopy. Serrated stress-strain behavior was observed in the curves obtained at 200 to 700 °C, which was associated with the dynamic strain aging effect. The yield strength and the elongation values show an anomalous behavior as a function of the test temperature. An intergranular cracking was observed specimen tensile tested at 500 °C that can be attributed to the decohesion of the carbides along the grain boundaries. The fracture surface of the specimen tensile tested at 700 °C showed the predominance of transgranular cracking with tear dimples with a parabolic shape.
Titanium nanotubes have attractive morphological and physicochemical properties for several applications, such as high surface area, mesoporous structure, good stability, ion exchange capacity, and antibacterial property. Therefore, the field of nanotube applications is increasingly expanding, such as in solar cells sensitized by dye, photocatalysis, and antibacterial activity, among others. Therefore, a study of the antibacterial properties of sodium titanate nanotubes (Na-TiNTs) was carried out together with physicochemical characterizations, such as Raman spectroscopy which shows a peak characteristic of Na-O-Ti from nanotube-agglomerated regions. The XRD diffractogram confirmed the Raman spectra and evidenced the crystalline structure associated to Na-TiNT, which showed the characteristic peaks of the sodium trititanate crystal. SEM and TEM images showed the morphology of hollow nanotubes and forming semispherical particles. EDS shows the percentage values of each of the compounds in the Na-TiNT. The bacterial activity of the Na-TiNT was analyzed in Escherichia coli, Staphylococcus aureus, and Pseudomonas aeruginosa. Na-TiNT modified the activity of the gentamicin and norfloxacin antibiotics against multiresistant strains. Synergistic effects against Gram-positive S. aureus 10 and Gram-negative P. aeruginosa 15 bacteria were observed when the Na-TiNT was associated with gentamicin, reducing the concentration of this antibiotic that is required to inhibit bacterial growth. Another synergic effect was observed for S. aureus 10 with norfloxacin.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.