Solidification of a chitosan-glycerol phosphate/blood implant in microfracture defects improved cartilage repair compared with microfracture alone by increasing the amount of tissue and improving its biochemical composition and cellular organization.
Bone marrow stimulation is performed using several surgical techniques that have not been systematically compared or optimized for a desired cartilage repair outcome. In this study, we investigated acute osteochondral characteristics following microfracture and comparing to drilling in a mature rabbit model of cartilage repair. Microfracture holes were made to a depth of 2 mm and drill holes to either 2 mm or 6 mm under cooled irrigation. Animals were sacrificed 1 day postoperatively and subchondral bone assessed by histology and micro-CT. We confirmed one hypothesis that microfracture produces fractured and compacted bone around holes, essentially sealing them off from viable bone marrow and potentially impeding repair. In contrast, drilling cleanly removed bone from the holes to provide access channels to marrow stroma. Our second hypothesis that drilling would cause greater osteocyte death than microfracture due to heat necrosis was not substantiated, because more empty osteocyte lacunae were associated with microfracture than drilling, probably due to shearing and crushing of adjacent bone. Drilling deeper to 6 mm versus 2 mm penetrated the epiphyseal scar in this model and led to greater subchondral hematoma. Our study revealed distinct differences between microfracture and drilling for acute subchondral bone structure and osteocyte necrosis. Additional ongoing studies suggest these differences significantly affect long-term cartilage repair outcome. ß
At twelve months, BST-CarGel treatment resulted in greater lesion filling and superior repair tissue quality compared with microfracture treatment alone. Clinical benefit was equivalent between groups at twelve months, and safety was similar.
An in vivo rat cage implant system was used to identify potential surface chemistries that prevent failure of implanted biomedical devices and prostheses by limiting monocyte adhesion and macrophage fusion into foreign-body giant cells while inducing adherent-macrophage apoptosis. Hydrophobic, hydrophilic, anionic, and cationic surfaces were used for implantation. Analysis of the exudate surrounding the materials revealed no differences between surfaces in the types or levels of cells present. Conversely, the proportion of adherent cells undergoing apoptosis was increased significantly on anionic and hydrophilic surfaces (46 ؎ 3.7 and 57 ؎ 5.0%, respectively) when compared with the polyethylene terephthalate base surface. Additionally, hydrophilic and anionic substrates provided decreased rates of monocyte͞macro-phage adhesion and fusion. These studies demonstrate that biomaterial-adherent cells undergo material-dependent apoptosis in vivo, rendering potentially harmful macrophages nonfunctional while the surrounding environment of the implant remains unaffected.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.