In this paper, the possibility of color controlling anodic titanium oxide by changing anodizing conditions of titanium in an ethanol-based electrolyte is demonstrated. Colored anodic titanium oxide was fabricated in an ethanol-based electrolyte containing 0.3 M ammonium fluoride and various amounts of deionized water (2, 3.5, 5, or 10 vol%), at voltages that varied from 30 to 60 V and at a constant anodization temperature of 20 °C. Morphological characterization of oxide layers was established with the use of a scanning electron microscope. Optical characterization was determined by measuring diffusion reflectance and calculating theoretical colors. The resulting anodic oxides in all tested conditions had nanotubular morphology and a thickness of up to hundreds of nanometers. For electrolytes with 3.5, 5, and 10 vol% water content, the anodic oxide layer thickness increased with the applied potential increase. The anodic titanium oxide nanotube diameters and the oxide thickness of samples produced in an electrolyte with 2 vol% water content were independent of applied voltage and remained constant within the error range of all tested potentials. Moreover, the color of anodic titanium oxide produced in an electrolyte with 2 vol% of water was blue and was independent from applied voltage, while the color of samples from other electrolyte compositions changed with applied voltage. For samples produced in selected conditions, iridescence was observed. It was proposed that the observed structural color of anodic titanium oxide results from the synergy effect of nanotube diameter and oxide thickness.
In this research, we attempted to modify the bandgap of anodic titanium oxide by in situ incorporation of selected elements into the anodic titanium oxide during the titanium anodization process. The main aim of this research was to obtain photoactivity of anodic titanium oxide over a broader sunlight wavelength. The incorporation of the selected elements into the anodic titanium oxide was proved. It was shown that the bandgap values of anodic titanium oxides made at 60 V are in the visible region of sunlight. The smallest bandgap value was obtained for anodic titanium oxide modified by manganese, at 2.55 eV, which corresponds to a wavelength of 486.89 nm and blue color. Moreover, it was found that the pH of the electrolyte significantly affects the thickness of the anodic titanium oxide layer. The production of barrier oxides during the anodizing process with properties similar to coatings made by nitriding processes is reported for the first time.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.