Rat and human bone marrow cells (BMCs) were cultured on a composite ceramic of zinc-containing beta-tricalcium phosphate and hydroxyapatite (ZnTCP/HAP) with a (Ca+Zn)/P molar ratio of 1.60 and varying zinc contents. After a 2-week culture of the BMCs in the presence of beta-glycerophosphate and dexamethasone, many macroscopic mineralized areas with high alkaline phosphatase (ALP) activity were seen on the ZnTCP/HAP ceramic disks. The ALP activity increased with increasing zinc content in the ceramics. The highest ALP activity was observed when the BMCs were cultured on the ceramics with 1.26 wt % zinc, and the ceramics released zinc ions at concentrations from 2.2 to 7.2 microg/mL into the culture medium. Zinc ions were incorporated into mineralized areas produced by BMCs. BMCs also were directly cultured onto the culture dish surface, and the addition of 100 microM of free ZnCl(2) (6.5 microg/mL) to the culture medium significantly increased the ALP activity of the BMCs relative to the culture medium without the ZnCl(2)addition. The maximum zinc concentration required to enhance mineralization was higher in human BMCs than in rat BMCs. The present study demonstrates the superiority of ZnTCP/HAP ceramics over TCP/HAP in supporting the osteogenic differentiation of BMCs, and thus these ceramics are safe and useful in clinical settings, such as for bone reconstructive surgery.
The in vitro and in vivo osteoblastic differentiation of rat bone marrow stromal cells (MSCs) was assessed on hydroxyapatite disks with 3 different porosities: 30%, 50%, and 70% (HA30, HA50, and HA70, respectively). MSCs obtained by 10-day culture of fresh bone marrow cells were subcultured for 2 weeks on 3 kinds of porous HA disks in the presence and absence of dexamethasone (Dex). After 2 weeks of subculture, alkaline phosphatase (ALP) activity and osteocalcin production of MSCs/HA composites with Dex were higher than those without, and increased with increasing porosity. The resultant bone tissue grafts "cultured-bone/HA constructs" were implanted subcutaneously into the backs of syngeneic rats, and harvested 1, 2, and 4 weeks after implantation. At 1 week, only cultured-bone/HA70 constructs exhibited expanded bone formation. At 2 and 4 weeks, active osteoblasts and progressive bone formation were observed morphologically in both cultured-bone/HA50 and HA70 constructs. At 4 weeks, bone tissue was observed even in cultured-bone/HA30 constructs. ALP activity and osteocalcin production also increased with increasing porosity and time after implantation. In this in vivo model, different scaffold porosity with similar crystal morphology of the apatite phase demonstrated marked differences in ability to support osteogenesis by implanted rat MSCs.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.