A novel strategy for fabricating nanoimprint templates with sub-10 nm patterns is demonstrated by combining electron beam lithography and atomic layer deposition. Nanostructures are replicated by step-and-repeat nanoimprint lithography and successfully transferred into functional material with high fidelity. The process extends the capacity of step-and-repeat nanoimprint lithography as a single digit nanofabrication method. Using the ALD process for feature shrinkage, we identify a size dependent deposition rate.

Sloped and stepped 3D structures were added to surface-patterned resists using grey-scale electron beam lithography and thermal reflow. A poly(methyl methacrylate) resist with moderate initial molecular weight of 120 kg/mol was chosen, which enabled processing with both nanoimprint and electron beam lithography. Using proper exposure doses, a molecular weight distribution was generated that allowed a selective thermal postprocessing of the exposed steps while the imprinted gratings on top of the resist were preserved. This allows fabricating mixed structures of microprisms surrounded by large-area nanogratings in the same resist layer. Working stamps were casted from the template pattern and subsequently replicated using thermal nanoimprint. As a possible application, backlight devices with arrays of light outcoupling prisms can be seen. V

Novel 3D resist structures are generated with both smooth slopes and stepped resist profiles on the same substrate and in very close vicinity. By performing gray-scale electron-beam exposure and development steps twice with different dose ranges, a selective transformation of multilevel structures into continuous slopes upon thermal treatment was enabled. The molecular weight dependence was analyzed and related to the locally different ability of the resist to flow, which enables one to selectively address resist structures which should be altered while others stay unaffected. The technique has large potential for prototyping elements and devices and can be used to fabricate stamps with complex 3D surface patterns for fabrication using nanoimprint. V

No abstract